高力ボルト綱中の水素拡散に及ぼす焼入れ焼もどし組織

スポンサーリンク

概要

• 論文の詳細を見る

• The effects of quenched and tempered microstructures on the diffusion coefficient and solubility of hydrogen in high tensile strength bolt steel have been investigated by means of the electrochemical permeation technique. The results obtained are as follows : (1) The diffusion coefficient was minimum when the steel had the as-quenched martensitic structure or the low temperature tempered martensite, and it increased with increasing tempering temperature. The mixed structure of ferrite and lamellar pearlite obtained by furnace cooling from a temperature above Ac_3 gave a higher diffusion coefficient than the tempered spheroidal pearlite. On the other hand, the solubility of hydrogen showed a behavior opposite to the diffusion coefficient. (2) The low diffusion coefficient and high solubility are attributed predominantly to hydrogen trapping at the lattice imperfections, such as dislocations and faults etc., which were introduced by martensitic transformation during quenching. (3) With regard to the effect of cathodic current density, i. e., the hydrogen concentration directly below the surface on hydrogen diffusion in tempered steel, the diffusion coefficient hardly depended upon the hydrogen concentration but the solubility of hydrogen increased up to a certain value with increasing cathodic current density. On the other hand, the hydrogen permeation current efficiency decreased with increasing cathodic current density. (4) The activation energies for hydrogen diffusion in the tempered martensite, tempered fine and/or spheroidal pearlites in the temperature range of 6 to 61℃, were almost constant (about 8. 1 kcal/mol) but the pre-exponential factor increased with tempering temperature. The heats of solution of hydrogen in the tempered martensite and tempered pearlites were almost the same (about - 10. 3 kcal/mol) , indicating the exothermic reaction. However, the pre-exponential factor decreased with increaing tempering temperature.

• 社団法人日本材料学会の論文
• 1981-02-15

著者

• 高尾 慶蔵

  長崎大学工学部材料工学科

• 坂本 芳一

  長崎大学工学部

• 大渕 一見

  長崎大学工学部

• 高尾 慶蔵

  長崎大工

関連論文

• 電析法による強磁性金属ナノワイヤーの作製
• 合金工具鋼中の水素拡散に及ぼす焼入れ焼戻し組織
• 炭素鋼中の水素拡散に及ぼす焼入れ焼戻し組織の影響
• 室温付近における銅中の水素の拡散および溶解
• 冷間圧延したPd中の水素トラップの一考察
• 高力ボルト綱中の水素拡散に及ぼす焼入れ焼もどし組織
• PC鋼中の水素拡散に及ぼす焼入れ焼戻し組織
• ニッケル電着時の水素透過に及ぼす添加剤の影響
• 21/4Cr-1 Mo鋼中の水素拡散に及ぼす焼入れ焼もどし組織(X線材料強度小特集)
• 各種構造用合金鋼中の水素拡散と焼入れ焼戻し組織
• トリポリリン酸ソ-ダを含む硫酸塩浴からのCu-Zn合金の電析
• エチレンジアミン浴からのCu-Zn合金の電析
• 構造用高張力鋼中の水素核酸に及ぼす焼入れ焼もどし組織の影響 (X線材料強度小特集)

もっと見る 閉じる

スポンサーリンク