Fe-Si 合金の定電位分極特性に関する研究
スポンサーリンク
概要
- 論文の詳細を見る
The anodic behavior of Fe-Si alloys containing 2~22% Si in deaerated H_2SO_4 solution (20℃) was studied by the potentiostatic method. The effects of the Si content on the corrosion potential E_<corr.>, passivation potential E_p, passivation current density I_p and passive current density i_k were determined. The effects of chloride ion on the passivity of some high Si alloys were also studied. The results are summarized as follows. (1) The effect of Si addition on the corrosion potential of iron is not so remarkable : it shifts slightly in negative direction when Si content is 2~6%, but the shift is in positive direction when Si content is 12~16%. (2) Low Si alloys (2~8% Si) exhibit polarization behaviors similar to that exhibited by iron except that their passive current densities are considerably higher than that of iron. (3) High Si alloys especially containing over 15% Si have an excellent passivating ability, i.e. more negative value of E_q and very low values of I_p and i_k. Also these alloys are characterized by the large difference between the potential of passivation and that of the complete passivation. From this behavior of passivation, it is suggested that silicon contributes greatly to passivation in case of high behavior of passivation, it is suggested that silicon contributes greatly to passivation in case of high Si-Fe alloys containing over 12% Si and the mechanism of passivation of these alloys differs from those of iron and low Si alloys. (4) During the active di ssolution of high Si alloys such as 15% Si-Fe, the preferential dissolution of iron occurs, and the corrosion current decrease remarkably with time until it drops as low as i_k value, but the potential shifts only slightly in the positive direction, showing that the passivity is not attained. (5) The flade potential of 15% Si alloy shows the value of +0.29V (S.C.E) as a clear arest on the potential decay curve. It is more negative than E_<ps%gt; (+0.38V), but far more positive than E_p (About-0.2V). (6) The effect of chloride ion in case of high Si alloys, appears as the continuous increase of passive current density with increasing chloride ion concentration without being accompanied by pitting corrosion within the scope of our experiments.
- 社団法人日本材料学会の論文
- 1968-08-15
著者
関連論文
- おがくずを利用したウッドセラミックスの調製について
- 複合めっき法による傾斜機能皮膜の形成について
- アルミニウム合金の粉末化による微細組織の調整
- 積層圧延および後熱処理によるFe-Al系金属間化合物相の生成挙動
- 積層圧延および後熱処理によるFe-Al系金属間化合物相の生成挙動
- 溶射法による傾斜機能皮膜の調製に関する研究
- 溶射法によるTiAL_3組成皮膜の調整について
- ウッドセラミックスの機械的性質におよぼす木材組織の影響について
- 溶射法による傾斜組織皮膜の調整について
- 407 ステンレス鋼へのケイ素とクロムの拡散浸透処理
- Tiインサート金属を用いたSiCとCuとのパルス通電接合
- Ni_Pめっき皮膜の時効硬化特性と脆性について
- 粉体状浸炭防止剤の開発とその性能について (特集 マルチメディアと先端技術)
- Fe-Si 合金の定電位分極特性に関する研究
- 銀複合接点の繊維溶浸法による調製と性質
- 多量に化合物を晶出したMg合金の開発(II)
- 多量に化合物を晶出したMg合金の開発(I)