V_2O_5-SrO-Sb_2O_3系ガラスの酸素感ガス特性
スポンサーリンク
概要
- 論文の詳細を見る
Oxygen gas sensing properties in dc conductivity of a semiconductive glass in the system V_2O_5 SrO Sb_2O_3 with a composition V_2O_5 : SrO : Sb_2O_3=73 : 18 : 9 (mol%) were investigated in flowing oxygen and ar gon gases at temperatures between 433 and 439 K. The conductivity was lower in O_2 and higher in Ar than that in air. This was attributable to changes in the concen tration of V^<4+> ion as a function of oxygen partial pres sure. Changes in conductivity by switching the flowing atmosphere between O_2 and Ar gases were found to be reproducible. Sensitivity of 4.5 (433K) was obtained to 100% oxygen. The dynamic changes in conductivity by switching the flowing atmospheres were well ex plaplained by an oxygen diffusion and desorption model.
- 社団法人日本セラミックス協会の論文
- 1994-04-01
著者
-
坂田 浩伸
東海大学工学部工業化学科
-
天野 正武
東海大学工学部工業化学科
-
天野 正武
東海大工
-
川島 康之
東海大学工学部化学科
-
岡本 哲也
東海大学工学部化学科
-
坂田 浩伸
東海大 工
-
岡本 哲也
東海大学工学部化学科:(現)電気化学工業
-
川島 康之
東海大学工学部化学科:(現)(株)オハラ
-
坂田 浩伸
東海大学工学部
関連論文
- V_2O_5-Bi_2O_3-TeO_2系ガラスの構造
- Fe_2O_3-PbO-Bi_2O_3系ガラスの電気伝導
- Fe_2O_3-Sb_2O_3-TeO_2系ガラスの電気伝導
- Bi_2O_3-SrO-V_2O_5系ガラス及び結晶化ガラスの電気的性質
- Sb_2O_3-SrO-V_2O_5系ガラス及び結晶化ガラスの電気的性質
- 2D09 Sb_2O_3-SrO-V_2O_5 系ガラスの作成と電気的性質
- ITO 膜の高温低効率における熱履歴現象
- 加熱・振動によるプリント配線板上はんだの回収
- V_2O_5-CaO-Bi_2O_3系ガラスの電気伝導
- V_2O_5-SrO-Sb_2O_3系ガラスの酸素感ガス特性