MgO-ZrO_2焼結体の機械的強度に及ぼす粒径の影響
スポンサーリンク
概要
- 論文の詳細を見る
Cubic- and tetragonal-ZrO_2-MgO composite ceramics were prepared by the pressureless sintering at 1650℃ for 4 h and 1350℃ for 24 h respectively, and the effect of grain size and ZrO_2 phase on bending strength (at room temperature and 1200℃) was investigated. The bending strength at room temperature of ZrO_2-MgO composite ceramics increased with increasing ZrO_2 content, because the grain size of MgO decreased with ZrO_2 addition. But the effect of ZrO_2 phase on the bending strength at room temperature was not recognized. In the case of bending test at 1200℃, when grain size of MgO was below 6 μm, specimens deformed plastically before breakage, and the yield stress at 1200℃ of c-ZrO_2-MgO was larger than that of t-ZrO_2-MgO, and fracture stress increased with decreasing the grain size of MgO.
- 社団法人日本セラミックス協会の論文
- 1992-02-01
著者
-
寺井 健二
宇部興産(株)
-
神徳 泰彦
宇部興産(株)
-
西田 明生
宇部興産(株)研究開発本部宇部研究所無機材料研究部
-
福田 真史
宇部興産(株)研究開発本部
-
西田 明生
宇部興産(株)宇部研究所
-
神徳 泰彦
宇部興産株式会社
-
西田 明生
宇部興産(株)
関連論文
- 一方向強化Si-Ti-C-O繊維結合型セラミック複合材料の引張破壊過程の観察とシミュレーション(実験計測技術の新展開)
- Si-Ti-C-O繊維結合型セラミックスの力学的特性に及ぼす繊維体積率の影響
- Si-Ti-C-O繊維結合型セラミックスの機械的性質に及ぼす境界炭素層の影響
- 水熱合成法によるPZT/PSZT多層膜の作製
- 気相法によるマグネシア粉末の合成とその性質(粉体小特集)
- MgO質燒結体の曲げ強度に及ぼす粒子径と表面粗さの影響
- MgO質焼結体の曲げ強度に及ぼす粒子径と人口欠陥寸法の影響
- MgO-ZrO_2焼結体の性質に及ぼす熱処理の影響
- 3H17 MgO 焼結体の微構造と機械的性質に及ぼす Y_2O_3 添加の効果
- MgO-ZrO_2焼結体の機械的強度に及ぼす粒径の影響
- スラリー特性に及ぼすバインダー吸着量の影響
- 1-ブタノールを結晶化調整剤として合成したアルミノフェリシリケートの触媒性能
- 1-ブタノールを結晶化調整剤とする ZSM-5型 鉄 - アルミノシリケート合成とメタノールからの低級オレフィン合成
- 一方向凝固Al_2O_3/Er_3Al_5O_共晶複合材料の高温強度と熱的安定性
- 一方向凝固Al_2O_3/YAG複合材料の製造と高温特性
- 窒化ケイ素 - イミド熱分解法
- 真珠岩の発泡性に及ぼす加熱雰囲気の影響
- 高純度マグネシア焼結体の機械的性質に及ぼす粒子径の影響
- 気相法マグネシア粉末の焼結性
- 扁平な高融点金属粒子Mo, Ta, Nbのミクロ分散によるAl_2O_3複合材料の靭性改善
- 窒化ケイ素粉末の結晶化度測定方法
- Si-Ti-C-O 繊維結合型セラミックスの微細構造と特性(セラミックス)
- 気相法高純度超微粉単結晶マグネシア及び高純度マグネシア焼結体