Al_2O_3-TiO_2ゾル-ゲル系の結晶化挙動
スポンサーリンク
概要
- 論文の詳細を見る
Al_2O_3-TiO_2 thin films and powder were synthesised from acid catalyzed sols of aluminium and titanium alkoxides containing acetyl acetone as a chelating agent. The crystallization of the system was studied as a function of the relative compositions and the firing temperature. Films of four different alumina-titania compositions (10, 20, 30 and 40 mol% alumina) were prepared and fired at various temperatures in the range from 300 to 1000℃ . The films and powders were amorphous, at any composition, up to about 600℃. Larger molar contents of Al_2O_3 were found to have an inhibitory effect on the crystallization of TiO_2, while larger contents of TiO_2 had only a weak influence on Al_2O_3 crystallization. The formation of a metastable β-Al_2TiO_5 phase was observed in films at 1000℃.
- 社団法人日本セラミックス協会の論文
- 1999-10-01
著者
-
TRAVERSA Enrico
Dipartimento di Scienze e Tecnologie Chimiche, Universita di Roma"Tor Vergata," Via della Ricerca Sc
-
Traversa E
Univ. Roma “tor Vergata" Roma Ita
-
Traversa Enrico
Department Of Chemical Science And Technology University Of Rome "tor Vergata
-
Traversa Enrico
Dipartimento Di Scienze E Tecnologie Chimiche Universita Di Roma"tor Vergata " Via Della R
-
Traversa Enrico
Dipartimento Di Scienze E Tecnologie Chimiche Universita Di Roma "tor Vergata " Via Della
-
Traversa Enrico
Universita Di Roma"tor Vergata"dipartimento Di Scienze E Tecnologie Chimiche
-
Enrico Traversa
Department Of Chemical Sciences And Technology University Of Rome "tov Vergata
-
MARTUCCI Alessandro
Dipartimento di Ingegneria Meccanica, Settore Materiali, Universita di Padova
-
INNOCENZI Plinio
Auther for correspondence
-
Martucci Alessandro
Dipartimento Di Ingegneria Meccanica Settore Materiali Universita Di Padova
関連論文
- Development of chemically-stable proton conducting BZY electrolytes for SOFCs at WPI-MANA, NIMS
- SmFeO3の表面状態と電気的性質
- WO_3を電極補助相とする高温用電気化学NO_2センサー
- ペロブスカイト型酸化物LnFe03(Ln=La,Nd,Sm,Gd,and Dy)の表面状態とN02ガス応答
- ストロンチウムと鉄をドープしたコバルト酸ランタンの微粒子前駆体の合成と熱分析
- ホットフィラメントCVDを用いた窒化ケイ素基板上へのダイヤモンド合成
- LaMnO_3 Fine Powder Prepared by the Thermal Decomposition of a Heteronuclear Complex, LaMn(dhbaen)(OH)(NO_3)(H_2O)_4
- Preparation of Perovskite-type Lafe_Co_O_3 by Thermal Decomposition of Heteronuclear Complex, {La[Fe_Co_(CN)_6・4H_2O}X
- ゾル-ゲル法で作製した酸化チタン薄膜の感湿特性
- 非オーム性電極を持つZnO緻密焼結体の感湿特性
- Preparation and Characterization of Heteronuclear Hexacyano Complexes, Ln_xSm_ [Co (CN) _6]・nH_2O (Ln=La, Er, and Yb)
- Al_2O_3-TiO_2ゾル-ゲル系の結晶化挙動