C-B-Si繊維コーティングとSiC表面コーティングの併用による連続繊維強化セラミックスの耐酸化性向上
スポンサーリンク
概要
- 論文の詳細を見る
Continuous fiber-reinforced composite with an amorphous Si-N-C matrix was prepared by a polymer impregnation pyrolysis method by using C-B-Si coated silicon nitride fiber as reinforcement. This composite had a fairly high oxidation resistance due to the self-formed seal of B_2O_3-SiO_2 upon oxidation of the C-B-Si fiber-coating. Chemical vapor deposited (CVD) SiC was coated on the composite to further enhance its oxidation resistance. The composite using mono-layered C-B-Si fiber-coating without surface-coating showed a strength decrease from 1136 to 635 MPa upon oxidation at 1473 K for 720 ks. SiC surface coating of 10 μm thickness on the composite improved its strength after oxidation to 814 MPa. The composite using three-layered C-B-Si fiber-coating showed negligible strength decrease from 979 to 846 MPa even without surface-coating. On this better composite, the SiC surface-coating did not improve the oxidation resistance, but decreased the mass gain by oxidation to half.
- 社団法人日本セラミックス協会の論文
- 2001-06-01
著者
-
両角 宏喜
東燃(株)総合研究所:(現)日産自動車(株)日産テクニカルセンター
-
松本 和久
三井造船(株)技術開発本部玉野研究所
-
佐藤 清
東燃(株)総合研究所
-
舟山 徹
東燃(株)総合研究所
-
礒田 武志
東燃(株)総合研究所
-
藤岡 尚起
三井造船(株)機械制御技術開発センター
-
川村 憲明
東燃(株)総合研究所
-
松本 和久
三井造船(株)機械制御技術開発センター
-
佐藤 清
東燃(株)総合研究所:(現)(株)先端材料
-
舟山 徹
東燃(株)総合研究所:(現)クラリアントジャパン(株)lse事業部
-
川村 憲明
東燃(株)総合研究所:(現)先端材料
関連論文
- SES用船首フレキシブルシールの耐久特性に関する研究
- ポリシラザンをマトリックス原料に用いた繊維強化セラミックスの機械的特性に及ぼすマトリックスの結晶性の影響
- C-B-Si繊維コーティングとSiC表面コーティングの併用による連続繊維強化セラミックスの耐酸化性向上
- 熱硬化性ポリシラスチレン-ペルヒドロポリシラザン共重合体の合成と熱分解
- ベルヒドロポリシラザンより製造された窒化ケイ素繊維の引張強度
- 3種類のポリシラザン-ペルヒドロポリシラザン,ポリボロシラザン,メチルヒドロポリシラザン-のセラミックス複合材用マトリックス原料としての評価
- ポリアルミノシラザンの合成とその熱分解
- 高純度非晶質窒化ケイ素繊維の結晶化挙動
- ペルヒドロポリシラザン含浸法による窒化ケイ素質複合材料の製造
- 繊維強化SiC複合材料の高温特性
- 低酸素含有ポリボロシラザンの合成と熱分解