熱処理PC鋼棒のレラクゼーション性について : 鋼材関係に関する研究資料 : PC構造特集号

概要

論文の詳細を見る
For the prestressed concrete steel bar, a smaller amount of relaxation is required together with higher mechanical properties. We studied on the relaxation property of prestressed-concrete steel bars which had heat treated carbon steel, spring steel, and low alloy steel to 115 kg/mm^2 and 130 kg/mm^2 in ultimate strength. In the experiment, we observed that S 30 C, S 40 C, S 50 C relaxed over 3% for 20 hours under the initial stress of about 80% of actural yield strength, SAE1 041, SCr-2 relaxed 2 to 3% and SCM 2, SCM 4, SUP 9 relaxed about 1% As for the relation of the relaxation with mechanical properties, it is recognized that the amount of relaxation is inclined to decrease with the increases of ratio σ_S/σ_B and of elongation. It was concluded that, the steel bar which had tempered at high temperature and was sufficient in regard to mechanical properties, was excellent also from the view point of relaxation.
社団法人日本材料学会の論文
1962-12-15