Rotating bending and reversed flexure tests on mild steel coated with paints were carried out. Paints used were vinyl and oily ship bottom paints and zinc-rich paint (ZRP). The effectiveness of the impressed current cathodic protection on the painted surface was also examined. In the rotating bending, the fatigue limit was obtained for the specimens coated with vinyl or oily paint, but in the reversed flexure tests, the S-N curves of the painted specimens were similar to those of the bare metal in sea water and no definite fatigue limits were obtained. The difference in the S-N diagrams of the two test methods was probably due to the large deformation at the side edges of the specimen in the reversed flexure test. The S-N diagram of the ZRP coated specimens at relatively high stresses nearly coincided with those of the bare metal in the air, but at the stresses below the fatigue limit in the air, specimens fractured at a nearly equal number of reversals of stress. This might be due to the consumption of the protective ability of ZRP, judging from the change of the electrode potential of the specimens. The fracture of the specimen was protected by repeated painting. The application of the impressed current cathodic protection togather with the oily paint was very effective and the current densities necessary to protect corrosion were reduced to about one-twentith or-thirtith of those of the bare specimens cathodically protected.
- 社団法人日本材料学会の論文
- 1961-12-15
著者
関連論文
- 耐候性鋼板の腐食疲労
- 鋼の低サイクルランダム疲労に関する研究(第3報) : 回転曲げ疲労試験
- 鋼の低サイクルランダム疲労に関する研究(第2報) : 荷重系列の影響についての考察
- 鋼の低サイクルランダム疲労に関する研究
- 鋼の低サイクルランダム疲労に関する研究 : (第1報)装置ならびに予備的実験
- 低サイクル腐食疲労破壊に関する研究(第2報) : fatigue crackの成長について
- 低サイクル腐食疲労破壊に関する研究(第1報) : 回転曲げ試験
- 繰返し衝撃重疊下の低サイクル腐食疲労(第1報)
- 軟鋼の腐食疲労と塗料の効果
- 鋼材の応力腐蝕に関する研究(第1報) : 軟鋼及び溶接部の腐蝕疲労
- 木材の圧縮クリープ
- Corrosion-Fatigue of Mild Steel in Sea Water : (2) The Influence of the Mean Stress on the Fatigue-Strength