洋白線の疲労破壊における顕微鏡組織とかたさ変化
スポンサーリンク
概要
- 論文の詳細を見る
The authors have investigated upon the variation of hardness value and microstructure due to fatigue fracture in nickel silver wire. Both cold-drawn and low annealed specimens with 2 m/m in diameter were used. Also, Haigh-Robertson testing machine was used. The followings are the results obtained : (1) The cold-worked nickel silver wire may be decreased in hardness value due to fatigue fracture, but it is not affected by the amount of repeated stress. It would be because of the softening phenomena where the nonuniform worked structure may be turned into grain growth states due to the repeated stress. (2) The 600℃×1 hr annealed nickel silver wire may be increased in hardness value due to fatigue fracture but it is not affected by the amount of repeated stress. (3) The low annealed nickel silver wire may be increased or/and decreased in hardness value, which is governed by the amount of repeated stress and the annealing temperature.
- 社団法人日本材料学会の論文
- 1961-01-15
著者
関連論文
- 203 Al 被覆鋼より線の疲労試験について
- 204 強圧延加工した薄板銅合金ばねの機械的強度
- 202 タングステンワイヤロープの機械的強度
- 201 ステンレス鋼ワイヤロープの熱処理矯正
- 薄板Cu-Ni-Si合金ばねの機会的性質
- 116 コネクタ用フラットコードの屈曲疲れ試験(疲労き裂・実物疲労)
- 134 超硬およびタングステン細線の引張り, 疲れ, ねじり破面について
- 207 ステンレス鋼ワイヤロープの機械的強度に及ぼすプーリ曲げの影響
- 131 ウレタン系歯付ベルトの寿命試験
- 18-8系ステンレス鋼線の疲労強度に及ぼす繰返速度の影響について
- 18-8系ステンレス鋼線の加工および焼なましによる疲労強度について
- 洋白線の疲労破壊における顕微鏡組織とかたさ変化
- ばね用洋白線の加工および焼鈍しによる疲労強さについて
- 純銅線の回転曲げ疲労における硬さ変化について