In order to measure the temperature dependence of the dynamic modulus in crystalline high polymers at definite frequency, an apparatus was constructed, which was found to be very useful for analysis of temperature-dispersion curve of dynamic modulus, due to its high accuracy and rapid operation for measurements, adding to the advantage of constant frequency. Both ends of sample fiber or high polymer film are fixed to two strain gauges of unbonded type, one of which is used to transform the sinusoidal displacement into electrical quantity proportional to the displacement and the other is transducer of generated force. Absolute values of these electrical vectors representing force and displacement are adjusted to unity (full scale of voltmeter) and vector reduction are conducted by changing the connection of the output circuit of two strain gauges. By this operation the value of tan δ can be directly read off by the voltmeter. Regulation of the magnitude of vector is conducted conveniently by controling the input of strain gauges. Dynamic modulus, G', can also be calculated from the ratio of the input voltages of strain gauges, E_2/E_1, when the output voltages of them are regulated to be equal, G'=K(E_2/E_1), where K is a constant relating to the dimensions of samples and strain gauges. The main structural feature of this apparatus exists in that the vector reduction is conducted without amplifying the respective electrical output from two strain gauges proportional to force and displacement respectively. By this method the possibility of introducing experimental error based on the phase shifting effect from amplifier could be avoided. However, in order to make this possible, it was necessary to amplify very small output voltage (less than one micro volt) by using selective amplifier of the highest sensitivity. Another advantage of this apparatus must be cited : the reading of the output voltages of strain gauges is not necessary in absolute values but the relative values of them are satisfactory for determination of both values of tan δ and G'. This makes the measuring operation so rapid that the long time stability of the amplifier is not so serious, and high reproducibility of data can be realized. The measurements of tan δ and G' at one temperature need only several tens seconds. The temperature characteristics of viscoelasticity of several fibers over a wibe temperature range were measured with heating rate of 1℃/min., with high precision and reproducibility.
- 社団法人日本材料学会の論文
- 1959-04-15
著者
関連論文
- 大気圧プラズマ処理ポリオレフィン粉末とポリエステルとのブレンド(物質生命化学科)
- 固体鎖状高分子の誘電吸収の形について : 高分子のレオロジー : レオロジー特集号
- 高分子の誘電スペクトルに対する架橋ならびにブレンドの効果 : 高分子のレオロジー
- 結晶性高分子と非晶性高分子の誘電特性の比較 : 高分子レオロジー
- メタアクリル酸エステル系列重合体の誘電的性質 : 高分子レオロジー
- 誘電緩和現象における時間-温度換算法則の適用限界について : 高分子レオロジー
- 大気圧下窒素プラズマ処理したポリエチレン粉末とナイロン6とのリアクティブプロセッシング(物質生命化学科)
- 自由体積概念に基づく高分子混合系物性の記述
- ポリエチレン単結晶集合体の粘弾性挙動 : 高分子固体のレオロジー
- 栗山捨三先生 KURIYAMA Sutezo -高貴の資質と炎の情熱-
- 私の心に生きる堀尾正雄先生
- 閉塞からフローの時代へ
- 結晶性高分子の微細構造と粘弾性吸收 : 高分子レオロジー
- 結晶性高分子における張力-温度特性の粘弾性的意義 : 高分子レオロジー
- 直続式力学的tanδメーターの試作 : レオメーター
- 結晶性高分子における弾性率の温度分散曲線の解析 : 結晶性高分子の構造とレオロジー
- 高分子固体の押出しにおける塑性変形
- Co60γ線照射によるポリエチレン単結晶の橋かけに対する電子顕微鏡的研究
- 加硫シス-1, 4-ポリブタジエンゴムのミクロ不均一構造と粘弾性
- ポリマーブレンドの粘弾性特性と模型実験による検討 : 高分子のレオロジー
- 5a-D-1 結晶内の分子運動と変形
- 固体押出しにおける高分子材料の塑性変形
- 溶液から成長させた高分子結晶の粘弾性
- 5p-G-3 単結晶の形態変化
- ポリエチレン固体の高圧力による押出し
- ポリプロピレン繊維の粘弾吸収と微細構造 : 高分子のレオロジー : レオロジー特集号
- 高圧下の高分子の構造と物性
- 高分子固体物性の研究 (日本の高分子が歩んだ道-2-高分子科学の発展をふりかえって)
- 高分子物性 (高分子科学と技術の新領域)
- 単結晶構造に基いた高分子物質の力学的性質 実験的方面 (高分子の単結晶(特集))
- マテリアル・キャラクタリゼ-ションとは(キャラクタリゼ-ション入門講座-8-)
- 結晶性高分子の温度分散
- 溶融粘度
- タイトル無し
- タイトル無し