FATIGUE LIFE DISTRIBUTION AND ITS SIMULATION IN SPHEROIDAL GRAPHITE CAST IRONS
スポンサーリンク
概要
- 論文の詳細を見る
Statistical fatigue tests have been carried out using smooth specimens of a spheroidal graphite cast iron(SGI)with ferritic microstructure and the fatigue life distributions were examined.It was found that fatigue cracks were initiated from casting defects at the early stage of fatigue life and thus fatigue life could be regarded as crack growth life.The scatter in fatigue lives was primarily attributed to the scatter in casting defect size.The fatigue life prediction was performed using experimentally determined crack growth characteristics.The obtained results agreed well with the experimental data.From practical viewpoint, similar prediction was conducted using the growth characteristics for large cracks(CT specimen).When the crack opening stress was assumed to be zero, the prediction showed longer fatigue lives than the experimental data at high stress level, while a good agreement at low stress level.Furthermore, a Monte Carlo simulation was performed using measured distribution function of casting defect size, and the similar results were obtained.Additional fatigue tests were conducted on both pearlitic and bull's eye materials prepared with heat treatment of different SGI from ferritic SGI.It was found that the fatigue strength of both materials was almost the same and also similar to that of ferritic material.The distribution of casting defect size in pearlitic material agreed closely with that in ferritic material.This indicated that if the distribution of the sizes of casting defects from which crack was initiated were the same in different SGI's, then the fatigue strength would be independent of microstructure.
- 社団法人日本材料学会の論文
- 1996-03-15
著者
-
Ogawa Takeshi
Department Of Internal Medicine Institute Of Clinical Medicine The University Of Tsukuba
-
TOKAJI Keiro
Department of Mechanical and Systems Engineering, Gifu University
-
Tokaji Keiro
Department Of Mechanical Engineering Faculty Of Engineering Gifu University
-
Ogawa Takeshi
Departmen Of Orthopaedic Surgery Nihon University School Of Medicine
-
Ogawa Takeshi
Department Of Mechanical Engineering Faculty Of Engineering Gifu University
関連論文
- Fatigue Strength and Fracture Mechanisms of Porous Ceramics(Reliability Engineering in Materials and Structures)
- -391- EFFECTS OF NIFEDIPINE ON LEFT VENTRICULAR FUNCTION DURING EXERCISE IN PATIENTS WITH STABLE EFFORT ANGINA : RELATION OF ITS EFFICACY TO THE DEGREE OF CORONARY ARTERY DISEASE
- -388- PROGNOSTIC SIGNIFICANCE OF POSTEXERCISE ABNORMAL ELEVATION OF SYSTOLIC BLOOD PRESSURE IN PATIENTS WITH ISCHEMIC HEART DISEASE : COMPARISON WITH THAT OF EXERTIONAL "HYPOTENSION"
- -194-MYOCARDIAL PERFUSION PATTERNS DEMONSTRATED BY DIGITAL SUBTRACTION ANGIOGRAPHY
- Influences of Microstructure and Specimen Size on Creep Properties of Solders
- -0581-MECHANISMS OF MENTAL STRESS-INDUCED MYOCARDIAL ISCHEMIA
- A CASE OF DILATED CARDIOMYOPATHY WITH SLIGHT HYPOPLASIA OF THE LEFT ANTERIOR DESCENDING ARTERY DEMONSTRATED BY CORONARY ANGIOGRAPHY : THE 5th CONFERENCE ON CARDIOMYOPATHY
- 13) DETERMINANTS OF SUDDEN DEATH IN HYPERTROPHIC CARDIOMYOPATHY
- 2) EFFECTS OF CATECHOLAMINE ON ELECTROCARDIOGRAPHIC FINDINGS AND LEFT VENTRICULAR PERFORMANCE IN PATIENTS WITH APICAL HYPERTROPHIC CARDIOMYOPATHY
- -30-THE EFFECT OF PHYSICAL TRAINING ON THE AUTONOMIC NERVOUS FUNCTION AND ITS ROLES IN IMPROVING THE EXERCISE TOLERANCE IN PATIENTS WITH OLD MYOCARDIAL INFARCTION
- Numerical Study for Secure Communications Using the Chaotic Masking Method in Two Microchip Lasers : Optics and Quantum Electronics
- -0711- MITOCHONDRIAL GENE MUTATIONS IN PATIENTS WITH DILATED CARDIOMYOPATHY(PROCEEDINGS OF THE 59th ANNUAL SCIENTIFIC MEETING OF THE JAPANESE CIRCULATION SOCIETY)
- C-Reactive Protein is Related to Ongoing Myocardial Damage in Patients with Non-Ischemic Chronic Heart Failure(Heart Failure, Clinical 6 (M), The 69th Annual Scientific Meeting of the Japanese Circulation Society)
- Synchronization of Chaos in Two Microchip Lasers : Comparison between Two Master-Slave Types and a Mutually-Coupled Type
- Fatigue Crack Initiation and Early Growth Behavior of a Ferritic Stainless Steel in Laboratory Air and in 3%NaCl Aqueous Solution
- Outcome after surgeries for primary spinal sarcoma
- Prediction of Mechanical Properties of Lead-free Solders Using Indentation Method
- THE MECHANISMS OF STRESS-INDUCED ST SEGMENT ELEVATION AND NORMALIZATION OF NEGATIVE T WAVES IN PATIENTS WITH PREVIOUS MYOCARDIAL INFARCTION : Ischemic Heart Disease (III) : III : 48 Annual Scientific Meeting, Japanese Circulation Society
- THE CHANGES OF INDICES OF MYOCARDIAL ISCHEMIA IN PATIENTS WITH EXERTIONAL CHEST PAIN AND ST DEPRESSION WHO HAVE NO SIGNIFICANT CORONARY ARTERY STENOSIS : Exercise Test : 46th Annual Scientific Meeting, Japanese Circulation Society
- MITOCHONDRIAL GENE MUTATIONS IN PATIENTS WITH HYPERTROPHIC CARDIOMYOPATHY
- Influence of silane coupling agent on the bonding of orthodontic brackets to porcelain teeth
- Effectiveness of bone marrow transplantation for revitalizing a severely necrotic small bone : experimental rabbit model
- Investigation of Effect of Pre-Strain on Very High-Cycle Fatigue Strength of Austenitic Stainless Steels
- FATIGUE STRENGTH AND FRACTURE MECHANISMS OF WC CERMET-SPRAYED STEEL
- Superior mesenteric arterial embolism : treatment by trans-catheter thrombo-aspiration
- Zeros of Partition Function and High Temperature Expansion for the Two-Dimensional Ising Models : Condensed Matter and Statistical Physics
- Critical Compressibility Factor of Two-Dimensional Lattice Gas : Kagome and Diced Lattices : Condensed Matter and Statistical Physics
- STATISTICAL DISTRIBUTION PATTERNS IN MECHANICAL AND FATIGUE PROPERTIES OF METALLIC MATERIALS
- FATIGUE LIFE DISTRIBUTION AND ITS SIMULATION IN SPHEROIDAL GRAPHITE CAST IRONS
- -0049-EFFECTS OF AGING AND CHROTHIC STRENUOUS EXERCISE ON MAXIMAL CARDIOVASCULAR FUNCTION
- Development of Super-brilliant Silver Metallic Coating
- Safety and Efficacy of Amlodipine A New Once-Daily Calcium Antagonist in Non-Hypertensive Patients with Coronary Artery Disease.:A New Once-Daily Calcium Antagonist in Non-Hypertensive Patients with Coronary Artery Disease
- Stereoselective synthesis of (-)-trachelanthic acid and (+)-viridifloric acid, necic acid components of pyrrolizidine alkaloids from a common intermediate.
- A Solubility Study of Coacervates of Magnesium, Calcium and Aluminum Highpolyphosphates in Acid Solutions