Recovery of Fast Neutron Irradiated Iron at Low Temperatures
スポンサーリンク
概要
- 論文の詳細を見る
The isochronal annealing studies of electrical resistivity of Fe after fast neutron irradiation at liquid helium temperature were performed. Recovery spectra of annealed, cold worked and as-received specimens were compared. The main peak in stage I was divided into two substages and stages II and III recovery seemed to be influenced by interstitial impurities.
- 社団法人日本物理学会の論文
- 1969-05-05
著者
-
Okuda Shigeo
Japan Atomic Energy Research Institute
-
Maeta Hiroshi
Japan Atomic Energy Research Institute
-
TAKAMURA Saburo
Japan Atomic Energy Research Institute
-
Takamura Saburo
Japan Atomic Energy Research Institue
関連論文
- c-Axis Spacing Changes in Pyrolytic Graphite after Neutron Irradiation at 5 K
- X-Ray Study of Neutron-Irradiated LiF Crystals
- Recovery of Fast Neutron Irradiated Iron at Low Temperatures
- Recovery of Fast Neutron Irradiated Copper and Gold at Low-Temperatures
- Recovery of Fast Neutron Irradiated Molybdenum at Low-Temperature
- Electrical Resistivity Measurements of Vanadium and Iron Deformed at 4.2°K
- Recovery of Fast Neutron Irradiated Niobium and Vanadium at Low Temperature
- Recovery of Low-Temperature Fast Neutron Irradiated Tungsten
- Recovery of Low-Temperature Fast Neutron Irradiated Tungsten
- Electrical Resistivity Measurements of Deformed Metals after Low Temperature Neutron Irradiation
- Effect of Plastic Deformation on the Low Temperature Recovery after Neutron Irradiation
- Electrical Resistivity Measurements of F.C.C. Metals Deformed at 4.2°K