Recovery of Fast Neutron Irradiated Molybdenum at Low-Temperature
スポンサーリンク
概要
- 論文の詳細を見る
The isochronal annealing studies of electrical resistivity of Mo after fast neutron irradiation at liquid helium temperature were performed. Recovery spectra of annealed and cold worked specimens were compared. An apparent change in stage I due to cold work was found.
- 社団法人日本物理学会の論文
- 1968-08-05
著者
-
Okuda Shigeo
Japan Atomic Energy Research Institute
-
Maeta Hiroshi
Japan Atomic Energy Research Institute
-
TAKAMURA Saburo
Japan Atomic Energy Research Institute
-
Takamura Saburo
Japan Atomic Energy Research Institue
関連論文
- c-Axis Spacing Changes in Pyrolytic Graphite after Neutron Irradiation at 5 K
- X-Ray Study of Neutron-Irradiated LiF Crystals
- Recovery of Fast Neutron Irradiated Iron at Low Temperatures
- Recovery of Fast Neutron Irradiated Copper and Gold at Low-Temperatures
- Recovery of Fast Neutron Irradiated Molybdenum at Low-Temperature
- Electrical Resistivity Measurements of Vanadium and Iron Deformed at 4.2°K
- Recovery of Fast Neutron Irradiated Niobium and Vanadium at Low Temperature
- Recovery of Low-Temperature Fast Neutron Irradiated Tungsten
- Recovery of Low-Temperature Fast Neutron Irradiated Tungsten
- Electrical Resistivity Measurements of Deformed Metals after Low Temperature Neutron Irradiation
- Effect of Plastic Deformation on the Low Temperature Recovery after Neutron Irradiation
- Electrical Resistivity Measurements of F.C.C. Metals Deformed at 4.2°K