Magnetic Properties of Mn_3B_4
スポンサーリンク
概要
- 論文の詳細を見る
Magnetic susceptibility of Mn_3B_4 with D7_b type structure was measured in the temperature range from liq. N_2 temperature to c.a. 900°K. Magnetic characteristic of Mn_3B_4 is assured to be antiferromagnetic and shows a sharp peak at 392°K. Experimental results suggest that an antiferromagnetic ordering in this phase consists of a +-+- stacking of ferromagnetic layers. An abrupt decrease in magnetic susceptibilities was observed below 226°K, and is ascribed to a transition to canted or conical screwed ordering in the layers.
- 社団法人日本物理学会の論文
- 1965-09-05
著者
-
Yanase Akira
Research Department Wireless Division Matsushita Electric Industrial Co. L.t.d.
-
HIROTA Hozumi
Research Laboratory, Wireless Division Matsushita Electric Industrial Co., Ltd.
-
Hirota Hozumi
Research Laboratory Wireless Division Matsushita Electric Industrial Co. Ltd.
-
HIROTA Hozumi
Research Laboratory, Wireless Division, Matsushita Electric Industrial Co., Ltd.
関連論文
- The Crystalline Anisotropy Energy in CrO_2
- Magnetic Properties of Chromium Oxide Modified by Vanadium Oxide
- Magnetic Properties of Fe-Modified Mn_3B_4
- Ferro- and Antiferromagnetism in (Mn_Cr_x)_3B_4
- Ferrimagnetic Resonance in Mn_2Sb
- Magnetic Properties of τ Phase in Co-Al-B and Co-Sn-B Systems
- Magnetic Properties of Mn_3B_4
- Magnetic Properties of Mn_Ni_xB_4 and Mn_Co_xB_4
- Mechanism of Disaccommodation in Ferrite