ほう化処理鋼すべり摩耗痕の観察について
スポンサーリンク
概要
- 論文の詳細を見る
The sliding wear tests were carried out under the condition of constant surface pressure without lubricant at room temperature, using the stationary test pieces of S45C borided steel and the rotary test pieces of low carbon steel. Those tests were carried out with constant sliding distance under various sliding velocity. The scanning electron microscopy and X-ray microanalysis were employed to investigate the wear surface trace of borided steel. The experimental results indicated that the morphology of the wear surface trace largely depended upon the wear mechanism such as oxidative wear, mechanical wear or melting wear. It was concluded that the wear mechanism or the wear life of borided steel could be estimated to some extent with the observation of wear surface trace.
- 社団法人日本鉄鋼協会の論文
- 1980-04-01
著者
関連論文
- 移動する指示器による2点支持のストレートエッヂのたわみ(第7報)
- ほう化処理した鋼の高温酸化について
- ほう化処理鋼すべり摩耗痕の観察について
- ほう化処理鋼すべり摩耗痕の観察について
- ほう化処理した鋼のすべり摩耗特性について
- ホウ酸, ホウ酸カリウムによる銅の浸せきホウ化処理
- ほう化処理を施した引き抜きダイスの耐摩耗性
- ホウ化処理した鋼の耐食性について