ほう化処理した鋼の高温酸化について

スポンサーリンク

概要

• 論文の詳細を見る

• This paper deals with the study of the high temperature oxidation behavior of borided steel and boride at various temperatures and time in air. The low carbon steel was used as the material and the immersion boriding was done with boric acid and potassium borate as sources of boron supply. In the case of heating at high temperature in air, the borided steel was expected to be resistant up to about 700℃ while Fe_2B fully existed. The apparent activation energy 25.1 kcal/mol was obtained for oxide formation of the boride Fe_2B in the temperature range from 700℃ to 900℃ in air. Surface boride Fe_2B changed as follows with the high temperature oxidation : Fe_2B⟶Fe_2B⟶Fe_2B⟶Fe-Oxide α-Fe α-Fe Fe-B-Oxide Fe-Oxide Fe-B-Oxide

• 社団法人日本鉄鋼協会の論文
• 1978-08-01

著者

• 渋谷 佳男

  静岡県工業試験場

• 遠藤 隆

  静岡県工業試験場

関連論文

• ほう化処理した鋼の高温酸化について
• 81 鋳鉄のベーナイト変態について (I)(鉄鋼の加工および性質, 第 55 回講演大会講演大要)
• ほう化処理鋼すべり摩耗痕の観察について
• ほう化処理鋼すべり摩耗痕の観察について
• ほう化処理した鋼のすべり摩耗特性について
• ホウ酸, ホウ酸カリウムによる銅の浸せきホウ化処理
• ほう化処理を施した引き抜きダイスの耐摩耗性
• ホウ化処理した鋼の耐食性について

スポンサーリンク