低炭素アルミニウムキルド鋼の再結品集合組織に及ぼす中間析出処理の効果

概要

論文の詳細を見る
The maximum enhancement of {111}<110> plus {554}<225> components in the recrystallization texture of a low-carbon aluminum-killed steel sheet is attained when the process is so controlled that gives the minimum nucleation rate of recrystallization in the final annealing. Precipitation-annealing at an intermediate stage of cold rolling is found to be effective to give the minimum nucleation rate. It is concluded that the nucleation rate of recrystallization depends on the size and distribution of fine aluminum-nitride particles that precipitate preferentially on dislocations and the dislocation density of the matrix is an important factor to attain an appropriate state of precipitation for the inhibition of nucleation of recrystallized grains.
社団法人日本鉄鋼協会の論文
1974-10-01