製鋼過程に於ける鋼中の水素及窒素に關する研究 : 附鐵鋼中の水素分析法
スポンサーリンク
概要
- 論文の詳細を見る
The author studied the vacuum extraction process for the analysis of hydrogen only, and succeeded in finding a process, using a simple and compact furnace and large specimens. He also found that the selection of specimens is important. The analysis of hydrogen was made by this process, whilst the analysis proposed by the 19th Divisional Committee of the Institute for the Promotion of Science and Technology ("Gakujitsu Shinko-Kai") was applied to nitrogen. Thus, the variation of the contents of hydrogen and nitrogen in the course of steel-manufacturing was investigated, and the measures for reducing such elements were considered. The results of the experiments are outlined below : - (1) In the acid open hearth refining, more hydrogen exists in the melting-down period and it is reduced at the oxydizing stage, whilst at the latter half period there is again a tendency towards its increase and the quantity rapidly increases at the killing period and after discharge. Nitrogen reduces while the steel is boiling. (2) In the basic open hearth furnace, the quantity of hydrogen increases even in the oxidizing and boiling periods, whilst that of nitrogen is considerably reduced by the boiling action. (3) In the electric arc furnace, the variation of hydrogen is not distinct, but it increases in the reducing period and after being discharged. (4) In each meting process, the quantity of hydrogen before casting is generally 4.5-7.5cc/100g (0.0004-0.0007%). (5) The main cause of mixing hydrogen is due to gas, water, etc, which are contained in steelmaking materials, slag-making agents combustion gas, air, ladle and moulds. The boiling action is very effective for the extermination of nitrogen, but is not remarkable for that of hydrogen. (6) In ingots, more hydrogen and nitrogen exist at the top and bottom, but less at the middle. The difference is more remarkable in nitrogen. (7) The hydrogen in steel diffuses even at a normal temperature. In the range below 1, 000℃, it is quickest at a temperature immediately below the transformation point.
- 社団法人日本鉄鋼協会の論文
- 1937-10-25
著者
関連論文
- 不銹鋼合せ鈑の研究 (III)
- 不銹鋼合せ鈑の研究 (I) : 製造法の概要並に一般的性質
- 不銹鋼合せ鈑の研究 (II) : 合鈑の諸性質に及ぼす加熱の影響
- "クラッド・スチール"に就て-2-
- 熔融せる鐵鋼中に含有されるガスの測定方法
- 製鋼過程に於ける鋼中の水素及窒素に關する研究 : 附鐵鋼中の水素分析法
- 鐵鋼中のサンド分析方法に就て
- 1978 年の新年を迎えて
- 1977 年の新年に当つて
- 会長就任にあたつて
- 鋳鍛鋼品の大型化の展望
- 研究開発について
- 本邦鉄鋼鍛造技術の進歩
- 合金鐵の代りにマンガン及クロムを使用する電弧爐製鋼法
- 鋼中のガスに就て
- 燒入用油の劣化防止法
- 熔鋼の脱酸に關する二三の研究
- 鋼と水素との關係
- 製鋼過程に於ける鋼中の水素及窒素に關する研究(第 2 報) : 平爐精錬中の熔鋼への水素浸入機構
- 23) 製鋼過程に於ける鋼中の水素及窒素に關する研究(第 2 報) : 熔鋼中への水素浸入機構に就て(日本鐵鋼協會第拾八囘講演大會)
- 高周波電氣爐鋼の砂疵輕減に關する實驗
- 酸性平爐鋼のサンド並に白點に就て
- 24) 酸性平爐鋼のサンド並に白點に就て(日本鐵鋼協會第拾五囘講演大會)
- 鋼中の珪酸鹽摘出法