高温度抽出法による鐵鋼中の瓦斯量に就て
スポンサーリンク
概要
- 論文の詳細を見る
Several furnace gases are dessolved in iron and steel during melting and contained as several compounds, blow holes, or solid solution after solidification. In the present work the analysis of these gaseous elements was carried out by the vacuum fusion method using a high frequency induction furnace. The extraction of gases contained in a graphite crucible to be used in the experiment and in vacuum furnace should be complete as possible and hence the graphite crucible is heated in vacuum at 1, 700℃ for 3 hours under working of vacuum pump. In a blank test the amount of oxygen was decreased below 10mg as CO_2 in 15 min. The amount of reduction of several oxide Fe_2O_3 MnO_2 SiO_2 Al_2O_3 was determined. The sample was introduced into the crucible heated at 1, 550℃ and oxygen was extracted as CO. The oxygen in Fe_2O_3 and MnO_2 was extracted almost completely, but that in SiO_2 and Al_2O_3 about 96% and 86% respectively
- 社団法人日本鉄鋼協会の論文
- 1934-06-25
著者
関連論文
- 24) 鐵鋼中の含有瓦斯に關する研究(日本鐵鋼協會第拾四囘講演大會)
- 高滿俺大洲田鋼の加熱變化に及ぼす炭素の影響
- 鐵鋼中の含有ガスに關する研究 : (第 VIII 報)鋼塊内の水素氣泡の生成に就て
- 鐵鋼中の含有ガスに關する研究 (VI) : 鐵及び鐵合金の水素吸収
- 鐵鋼中の含有ガスに關する研究 : (第 V 報)熔融状態に於ける鐵の酸素溶解度並びに凝固時の酸素分離に就て
- 鐵鋼中の含有ガスに關する研究 (IV) : 眞空熔融法に依る鋼中酸素定量裝置の改良
- 高温度抽出法に依るフェロ・タングステン中の酸素定量に及ぼす鐵蒸發の影響
- 鐵鋼中の含有ガスに關する研究(第 2 報) : 眞空熔融法による鐵鋼中の酸素及窒素定量に就て
- 10) 鐵鋼中の含有瓦斯に關する研究(第 5 報) : 鐵及鐵合金の水素吸収に就て(日本鐵鋼協會第拾八囘講演大會)
- 鐵鋼中の含有瓦斯に關する研究(第 3 報) : 鋼塊内の水素分布及其の擴散に就て
- 23) 鐵鋼中の含有瓦斯に關する研究(第二報) : 鋼塊内の酸素分布に及ぼす炭素の影響(日本鐵鋼協會第拾五囘講演大會)
- 高温度抽出法による鐵鋼中の瓦斯量に就て
- 8) 高温度抽出法による鐵鋼中の瓦斯定量に就て(日本鐵鋼協會第拾壹囘講演大會)