冷間圧延したオーステナイト系ステンレス鋼の低温熱処理時の収縮
スポンサーリンク
概要
- 論文の詳細を見る
Austenitic stainless steel has good corrosion resistance because of its high chromium content. Moreover, it can be hardened significantly by cold-working, though it is not hardened by heat treatment. Cold rolled austenitic stainless steel is, therefore, widely applied in spring parts, transportation equipment, architectural materials and so on. However, this cold rolled austenitic stainless steel has the peculiar behavior during annealing at low temperature which is not observed in annealed stainless steel. (1) It contracts significantly parallel to the rolling direction during annealing without load. (2) Creep occurs at low stress below the proof strength. To study the mechanism of contraction, the effect of stability of austenite, hardness and martensite induced plasticity on contraction were investigated, and 30% reduced austenitic stainless steel was found to contract by 3∿17×10^<-4> during annealing. Contraction is considered to be connected with ε-martensite and stress relaxation.
- 社団法人日本鉄鋼協会の論文
- 1995-05-01
著者
関連論文
- 高純度フェライト系ステンレス鋼管の造管法とその成形性について
- 2相系ステンレス鋼のσ相の析出挙動に及ぼす成分の影響
- SUS 304 熱間圧延板の酸化挙動と脱スケール性に及ぼす焼鈍温度と雰囲気の影響
- Ni/304,Monel/304クラッド鋼の溶接部における凝固挙動
- SUS 304鋼スラブ中の介在物組成に及ぼす精錬スラグ組成の影響
- 619 19Cr-0.5Mo 鋼の相変態・炭化物析出挙動(ステンレス鋼の機械的性質, 軸受鋼, 鋳鉄, ロール, 材料, 日本鉄鋼協会第 114 回(秋季)講演大会)
- 698 フェライト系ステンレス鋼の熱間圧延時の再結晶挙動(ステンレス鋼, 材料, 日本鉄鋼協会第 104 回(秋季)講演大会)
- 冷間圧延したオーステナイト系ステンレス鋼の低温熱処理時の収縮
- 結晶粒微細化を利用した高強度SUS304の開発
- SUS430鋼中の炭化物析出に及ぼす熱延板焼鈍の影響
- 冷間圧延したオーステナイト系ステンレス鋼をレベラ矯正した時観察される収縮
- 冷間圧延したオーステナイト系ステンレス鋼をレベラ矯正した時観察される収縮
- 冷間圧延したオーステナイト系ステンレス鋼板の平たん化に及ぼす低温熱処理時の負荷応力の影響
- 冷間圧延したオーステナイト系ステンレス鋼の低温熱処理時の収縮
- 最近のステンレス板材