C-Mn-Nb 系熱延鋼板の機械的性質に及ぼす連鋳直接圧延条件の影響

概要

論文の詳細を見る
A study has been made of the effects of the conditions of direct hot rolling after continuous casting on the mechanical properties of hot rolled C-Mn-Nb steel sheets. The following results are obtained. (1) Austenite (γ) grain size after casting is very large compared with that after reheating at 1250℃ for 1h. Ferrite grain sizes after hot rolling are almost equal in both processes. This is probably because γ grain boundaries befor hot rolling do not contribute to the ferrite refinement because of their very low densities. (2) Tensile test results of steel sheets produced by both processes are almost the same if niobium is almost completely soluted before hot rolling. (3) In case, total hot rolling reduction after casting is higher than 40%, total elongation becomes very large. (4) Under the experimental condition of total hot-rolling reduction being 88%, the strengthening effect of niobium is saturated when niobium content is more than about. 0.035%. (5) The effects of the cooling rate in solidification (about 18 and 235℃/min at 1500-1300℃) and the heat history difference in the slab width on tensile properties are small in this direct hot rolling simulation test.
社団法人日本鉄鋼協会の論文
1986-12-01