高炭素オーステナイト系耐熱鋼の 1050℃クリープにおける析出物の変化

概要

論文の詳細を見る
A study has been made on the behavior of precipitates in niobium or titanium and niobium-containing centrifugal cast heat-resisting steels (HK40, HP and IN519) during creep rupture test at 1050℃. (1) In the as-cast condition, iron chromium carbide of M_7C_3 type precipitates, except for steel IN519 (0.33%C-24%Cr-24%Ni) where M_<23>C_6 type precipitates. Titanium niobium carbonitride (MX) precipitates in the steel containing titanium and niobium, and niobium carbonitride (NbX) precipitates in the steel containing only niobium. Chromium nitride (Cr_2N) precipitates except in the steel containing only niobium. (2) During creep rupture test, M_7C_3 in the as-cast steel changes to (Cr_<0.85>Fe_<0.15>)_<23>C_6. As the results of nitriding by air, Cr_2N increases and complex nitride, (Cr, Fe) NbN of tetragonal lattice, precipitates in the niobium-containing steel. Moreover, substitution reaction proceeds between carbon and nitrogen or between titanium and niobium with change of lattice parameter. (3) M_<23>C_6, Cr_2N and AIN are completely decomposed by hydrochloric acid (1+1) at 90℃. By the same acid M_7C_3, MX and NbX are decomposed gradually but (Cr, Fe) NbN is hardly decomposed. Based upon the differences in chemical stability of precipitates, the chemical composition and amount of each kind of precipitates can be successfully determined.
1983-01-01