シリコン含有鋼板の溶融亜鉛によるぬれ性に及ぼす酸化-還元条件の影響

概要

論文の詳細を見る
Effects of Si content in steel and the condition of partially-or non-oxidizing treatment followed by reduction treatment on dynamic wetting characteristics of Si-containing steels immersed in a molten zinc bath were studied by means of a partially-or non-oxidizing furnace simulator and a measureing instrument of gas reduction type meniscograph. 1) Steels containing 0.83% Si exhibited a good wettability when they were oxidized partially at an air/fuel ratio of 1.05 or more, which formed an oxide film of visible thickness and then reduced for 30 to 40s at 700℃. 2) The zinc wettability of Si-containing steels well corresponded to the degree of formation of Fe containing oxygen, namely Fe(O) and also the degree of Si enrichment at the steel surface layer which was composed of (FeO)_2 SiO_2. 3) The surface topography of steels changed in accordance with the air/fuel ratio during the partially-oxidizing treatment, Si content in steels and reduction treatment conditions. The rougher and more porous the surface morphology, the greater the initial wetting rate of the steels.
社団法人日本鉄鋼協会の論文
1982-12-01