純鉄の浮遊帯域精製効果について

概要

論文の詳細を見る
A study was made of the refining conditions for obtaining high purity iron from re-electrolytic iron by the floating zone melting technique. The main results obtained are summarized as follows : (1) The effect of the specimen diameter on the zone refining was not recognized in a range from 5 to 25 mm dia. (2) The later the travelling rate or the more the number of passage was, the greater the zone refining effect was. (3) A multiple zone refining which was alternately melted in dry H_2 and wet H_2 was very effective, and after seven zone passes in dry H_2, wet H_2 and vacuum the specimen showed the lowest value of resistance ratio (R_<4-2°K>/R_<295°K>=1/210). (4) From the zone refined specimen, only Co, Cu, Ni and Si were detected as the remained metallic impurities. O and N were effectively removed by zone melting in dry H_2 and wet H_2, but C was hardly removed even in wet H_2. (5) The overlap method was found to be effective technique, as compared with an usually zone refining method, for multiple zone refining to protect "melt in" or diffusion of impurities from the unpurified section adjacent to the starting end.
社団法人日本鉄鋼協会の論文
1971-03-01