鋳鋼の高温割れ傾向におよぼす諸元素の影響 (III) : Ti, Sn, As, Sb, Bi, Pb, O その他の元素の影響ならびに I∿III 報の総括
スポンサーリンク
概要
- 論文の詳細を見る
In the preceding two reports under the same heading as this, (Tetsu-to-Hagane Vol.40 (1954) p.979, Vol.43 (1957) p.1293) the author described the influence of C, Si, Mn, P, S, Cu and Al on hot-tearing tendency of cast steel. In this last report he describes the influence of Ti, Sn, As, Sb, Bi, Pb, O, H and N, and finally gives a summary of the whole series. The results are briefly summarized as follows : (1) Titanium has little effect on hot-tearng tendency of low sulphur steel, but it has the effect of increasing resistance to hot-tearing of high sulphur steel. It will be more economical and effective to use titanium together with aluminium than to use titanium separately. (2) Tin has a very bad effect on hot-tearing tendency of such steel that shows good resistance to hot-tearing before addition of tin. Addition of 0.1% tin is found to be clearly harmful. (3) Arsenic has a similar effect as tin ; 0.1% arsenic is found to be clearly harmful. (4) Antinomy has an even more harmful effect than tin or arsenic. (5) Bismuth too has a clearly bad effect on hot-tearing tendency of cast steel, though it is known that little or no bismuth is soluble in liquid iron. (6) Lead is found to have no effect on hot-tearing tendency of cast steel, and this may come from the fact that lead is not soluble in liquid iron. (7) Oxygen in steel has no direct effect upon hot-tearing tendency provided that oxygen content is not larger than usual value found in steel before deoxidation with silicon. However, it is conceivable that oxygen gives harm indirectly to resistance of high sulphur steel to hot-tearing, because oxygen causes loss of silicon and aluminium which reduce the hot-tearing caused by sulphur. (8) Bubbling water vapour through melt of steel is found to have little effect on hottearing tendency. This means that hydrogen too has little effect. (9) Nitrogen in steel seems to have little effect on hot-tearing tendency.
- 社団法人日本鉄鋼協会の論文
- 1958-01-01
著者
関連論文
- 第 46 回講演大會工場見學記
- 91 鉄鋼の 1100℃から溶融点に至る温度範囲におけるクリープの測定
- 91 鉄鋼の 1100℃から溶融点に至る温度範囲におけるクリープの測定(製鋼, 日本鉄鋼協会第 72 回(秋季)講演大会講演)
- 171 引張りを受ける凝固シェルの粒界液膜の厚み変化・圧力変化の解析(連鋳表面疵・内部割れ, 製鋼, 日本鉄鋼協会 第 105 回(春季)講演大会)
- 鋳鋼の高温割れ傾向におよぼす諸元素の影響 (III) : Ti, Sn, As, Sb, Bi, Pb, O その他の元素の影響ならびに I∿III 報の総括
- 鋳鋼の高温割れ傾向におよぼす諸元素の影響 (II) : 前報の補足ならびに Cu および Al の影響
- 50 鋳鋼の高温割れ傾向に及ぼす諸元素の影響 (V) Sn, As, Sb, Bi, Pb, O, H, N の影響(第 51 回講演大会講演大要)
- 小松製作所粟津工場(第 48 回講演大會工場見学記)
- 日曹製鋼富山工場(第 48 回講演大會工場見学記)
- 不二越鋼材富山製造所(第 48 回講演大會工場見学記)
- 廣貫堂(第 48 回講演大會工場見学記)
- 日産化学富山工場(第 48 回講演大會工場見学記)
- 鑄鋼の高温割れ傾向に及ぼす諸元素の影響 (I) : C, Si, Mn, P 及び S の影響
- 鑄鋼の高温割れ傾向の新試驗法
- 46 鑄鋼の高温割れ傾向に及ぼす諸元素の影響 (IV) : AI 及びその他の影響(日本鐵鋼協會第 46 囘講演大會講演大要)
- 45 鑄鋼の高温割れ傾向の新試驗法(日本鐵鋼協會第 46 囘講演大會講演大要)