鑄鋼の高温割れ傾向に及ぼす諸元素の影響 (I) : C, Si, Mn, P 及び S の影響
スポンサーリンク
概要
- 論文の詳細を見る
Two different shapes of test casting were used for determining hot-tearing tendency of cast steels. The first one comprised a 40mm diameter vertical cylinder and four horizontal, radial branches, each joined to the cylinder by a special design. The hot-tearing tendency of a steel was determined by fracturing these joints at room temperature. The test casting of the second type was a kind of plate casting, the thickness of its main part being 20mm. Length of hot-tear in this plate was taken as an index to hot-tearing tendency of the cast steel. Several spoonfuls of molten steel sample were taken from each heat of ordinary cast steel manufactured in a 5-ton basic arc furnace, and then each spoonful was tested after addition of various elements into the spoon. Again, the correlations between the analysis of each element and the resistance of steel to hot-tearing was studied by use of many heats of steel without any addition in the spoon. From results of studying on the influences of C, Si, Mn, P and S. followng conclusions were obtained : (1) Hot-tearing tendency increased with increase in the carbon content within the range of 0.16∿0.6%C. (2) Silicon did not seem to affect the hot-tearing tendency in a simple way, but a study on the correlation showed that steels containing 0.4∿0.5% silicon had the maximum resistance to hot-tearing. (3) Hot-tearing tendency decreased as the manganese content increased until the latter reached at least 0.75%, but it seemed to have a minimum point before the manganese content reaches 1%. (4) Even small additions of phosphorus were so detrimental that increase of the phosphorus from 0.02% to 0.04% had nearly the same effect as increase of the sulphur from 0.01% to 0.02%. (5) The wellknown fact that sulphur was the most deleterious element was accertained here again.
- 社団法人日本鉄鋼協会の論文
- 1954-10-25
著者
関連論文
- 第 46 回講演大會工場見學記
- 91 鉄鋼の 1100℃から溶融点に至る温度範囲におけるクリープの測定
- 91 鉄鋼の 1100℃から溶融点に至る温度範囲におけるクリープの測定(製鋼, 日本鉄鋼協会第 72 回(秋季)講演大会講演)
- 171 引張りを受ける凝固シェルの粒界液膜の厚み変化・圧力変化の解析(連鋳表面疵・内部割れ, 製鋼, 日本鉄鋼協会 第 105 回(春季)講演大会)
- 鋳鋼の高温割れ傾向におよぼす諸元素の影響 (III) : Ti, Sn, As, Sb, Bi, Pb, O その他の元素の影響ならびに I∿III 報の総括
- 鋳鋼の高温割れ傾向におよぼす諸元素の影響 (II) : 前報の補足ならびに Cu および Al の影響
- 50 鋳鋼の高温割れ傾向に及ぼす諸元素の影響 (V) Sn, As, Sb, Bi, Pb, O, H, N の影響(第 51 回講演大会講演大要)
- 小松製作所粟津工場(第 48 回講演大會工場見学記)
- 日曹製鋼富山工場(第 48 回講演大會工場見学記)
- 不二越鋼材富山製造所(第 48 回講演大會工場見学記)
- 廣貫堂(第 48 回講演大會工場見学記)
- 日産化学富山工場(第 48 回講演大會工場見学記)
- 鑄鋼の高温割れ傾向に及ぼす諸元素の影響 (I) : C, Si, Mn, P 及び S の影響
- 鑄鋼の高温割れ傾向の新試驗法
- 46 鑄鋼の高温割れ傾向に及ぼす諸元素の影響 (IV) : AI 及びその他の影響(日本鐵鋼協會第 46 囘講演大會講演大要)
- 45 鑄鋼の高温割れ傾向の新試驗法(日本鐵鋼協會第 46 囘講演大會講演大要)