熔銑の改良研究 (II) : 各種ガス吹込みについて
スポンサーリンク
概要
- 論文の詳細を見る
The changes in some properties of cast iron treated by blowing of various gases (N_2, coke gas, H_2, air, CO_2 and O_2) into the molten state were investigated. (1) By the blowing of reducing gases such as H_2 and coke gas, the fluidity of molten iron increased and the precipitation of flaky graphite was accelerated. The above mentioned phenomena were distinct in the B. F. iron containing of Ti, V and other impurities. (2) By the blowing of N_2, air and CO_2 gases into the B. F. iron, the fluidity decreased, but the changes in other properties of the iron were not nearly observed. On the other hand, in a charcoal iron the structure was changed into the non-uniform fracture with fine graphite and at the same time the fluidity and tensile strength decreased. (3) By the blowing of O_2 into B. F. irons, impurities such as Ti, V and etc. decreased, and moreover the mechanical properties were improved so as to show the character near to that of charcoal iron. (4) The cast iron made of charcoal iron was easily nodulized by magnesium treatment after the blowing of H_2 or coke gas, whereas that of B. F. irons containing the amount of impurities were more easily nodulized after the blowing of O_2. Perhaps the reason of this phenomena was as follows : it had been known that oxygen and impurities such as Ti, As, V and etc. prevented the nodulizing of graphite by magnesium. By the blowing of O_2 into B. F. irons containing the amount of impurities, some of the impurities decreased but the oxygen- content did not increased. On the other hand, as charcoal iron did not contain impurities, the deoxidation by reducing gases gave the good effect for nodulizing of graphite.
- 社団法人日本鉄鋼協会の論文
- 1956-01-01
著者
関連論文
- 82 高炉溶銑にて製造せる鋼塊鋳型について(製鋼・電気炉, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 201 硬鋼線材のオーステナイト結晶粒の調整について(性質, 日本鉄鋼協会第 69 回春季講演大会講演論文集 (II))
- 99 インゴットモールドに関する 2, 3 の研究(第 54 回講演大会講演大要)
- 244 連鋳硬鋼線の品質について(鋳造・加工・ウィスカー・組織・強度一般, 加工・性質・分析・計測, 日本鉄鋼協会第 80 回(秋季)講演大会講演)
- 熔銑の改良研究 (IV) : キユポラ熔湯への O_2 吹込の利用
- 40 熔銑の改良研究 (IV) : キュポラ熔湯への O_2 吹込の利用(第 51 回講演大会講演大要)
- 235 鋼の歪時効に関する 2, 3 の観察(性質・基礎, 性質, 日本鉄鋼協会第 73 回(春季)講演大会講演)
- 78 各種外国銑の化学成分と黒鉛球状化能について(鉄鋼の加工および性質, 第 55 回講演大会講演大要)
- 球状黒鉛鋳鉄用銑鉄製造ならびにこれら原料銑中の微量特殊元素の影響について
- 5 鋳鉄の黒鉛球状化におよぼす微量元素の影響について(第 53 回講演大会講演大要)
- 73 銑鉄に及ぼす Zn の影響について(第 51 回講演大会講演大要)
- 熔銑の改良研究 (I) : 酸素吹込について
- 10 酸素吹込による熔銑の改良(日本鐵鋼協會第 48 回講演大會講演大要)
- 57 銑鐵破面の不均一性について(日本鐵鋼協會第 47 囘講演大會講演大要)
- 47 真空溶解による溶鉄の脱砒について(製鋼・基礎・他, 日本鉄鋼協会第 64 回(秋季)講演大会講演大要)
- 熔銑の改良研究 (III) : 熔銑へのスケール添加と O_2 吹込み処理との比較
- 熔銑の改良研究 (II) : 各種ガス吹込みについて
- 58 熔銑の改良に関する研究 (III) : 熔銑へのスケール添加と O_2 吹込との比較(日本鐵鋼協會第 50 回講演大会講演大要)
- 10 熔銑の改良に関する研究 (II) : 各種ガス吹込について(第 49 回講演大会講演大要)
- 18 球状黒鉛鑄鐵に於ける組織の不均一性に關する一考察(日本鐵鋼協會第 44 回講演大會講演大要)