The effect of mill scale addition into molten iron was investigated in comparison with the oxygen blowing process as reported previously (Tetsu-to-Hagane, Vol.41, 1955, No.4, p.407). The scale was added at the high temperature (about 1450℃) into molten iron to decrease the undesirable effect of oxidation. As the results, it was found that by the treatment of adequate scale addition into molten iron the amount of Ti, and V in the iron decreased and so even the unsuitable irons as materials for ductile cast iron were easily nodulized by magnesium treatment after the scale addition, as well as in the case of oxygen blowing treatment. And also found that the above effects of the scale addition were inferior in comparison with the case of oxygen blowing treatment in which the temperature of molten iron rose remarkably.
- 社団法人日本鉄鋼協会の論文
- 1956-05-01
著者
関連論文
- 82 高炉溶銑にて製造せる鋼塊鋳型について(製鋼・電気炉, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 201 硬鋼線材のオーステナイト結晶粒の調整について(性質, 日本鉄鋼協会第 69 回春季講演大会講演論文集 (II))
- 99 インゴットモールドに関する 2, 3 の研究(第 54 回講演大会講演大要)
- 244 連鋳硬鋼線の品質について(鋳造・加工・ウィスカー・組織・強度一般, 加工・性質・分析・計測, 日本鉄鋼協会第 80 回(秋季)講演大会講演)
- 熔銑の改良研究 (IV) : キユポラ熔湯への O_2 吹込の利用
- 40 熔銑の改良研究 (IV) : キュポラ熔湯への O_2 吹込の利用(第 51 回講演大会講演大要)
- 235 鋼の歪時効に関する 2, 3 の観察(性質・基礎, 性質, 日本鉄鋼協会第 73 回(春季)講演大会講演)
- 78 各種外国銑の化学成分と黒鉛球状化能について(鉄鋼の加工および性質, 第 55 回講演大会講演大要)
- 球状黒鉛鋳鉄用銑鉄製造ならびにこれら原料銑中の微量特殊元素の影響について
- 5 鋳鉄の黒鉛球状化におよぼす微量元素の影響について(第 53 回講演大会講演大要)
- 73 銑鉄に及ぼす Zn の影響について(第 51 回講演大会講演大要)
- 熔銑の改良研究 (I) : 酸素吹込について
- 10 酸素吹込による熔銑の改良(日本鐵鋼協會第 48 回講演大會講演大要)
- 57 銑鐵破面の不均一性について(日本鐵鋼協會第 47 囘講演大會講演大要)
- 47 真空溶解による溶鉄の脱砒について(製鋼・基礎・他, 日本鉄鋼協会第 64 回(秋季)講演大会講演大要)
- 熔銑の改良研究 (III) : 熔銑へのスケール添加と O_2 吹込み処理との比較
- 熔銑の改良研究 (II) : 各種ガス吹込みについて
- 58 熔銑の改良に関する研究 (III) : 熔銑へのスケール添加と O_2 吹込との比較(日本鐵鋼協會第 50 回講演大会講演大要)
- 10 熔銑の改良に関する研究 (II) : 各種ガス吹込について(第 49 回講演大会講演大要)
- 18 球状黒鉛鑄鐵に於ける組織の不均一性に關する一考察(日本鐵鋼協會第 44 回講演大會講演大要)