高周波中斷燒入に關する研究
スポンサーリンク
概要
- 論文の詳細を見る
For the purpose of stress-relief in the induction surface-hardening the martempering was superior to the tempering at low temperature. However, the surface of martempered steel was stained with salt, therefore the martempering could not be applied to the induction surface-hardening. Fortunately, the induction surface-hardening was operated automatically by the magnetic relay. As soon as the water-cooling of the induction surface-hardening was stopped, before the induction heated specimen was completely cooled down to the temperature of water, this specimen was cooled in air or oil, and the effects similar to that of the martempering on the induction surface hardening were obtained. For this purpose, the experiments were carried out with a 0.44% C-0.92% Cr steel.
- 社団法人日本鉄鋼協会の論文
- 1954-06-25
著者
関連論文
- 軟鋼板電弧熔接に於ける酸素と炭素及酸素と滿俺との平衡に就て(第 1 報)
- 先天異常にかかわる難問題とその克服を目ざす歩み
- 先天異常にかかわる種々の難問題 : 現在と未来
- PC鋼棒ねじ部の力学的性質について
- ヒトの奇形発生に関する諸問題
- 139 転造した 13mmφ タップについて : タップの熱処理改善に関する研究 III(合金鋼その他, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 138 6mmφ タップの焼入成形について : タップの熱処理改善に関する研究 II(合金鋼その他, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 65 高周波中断燒入に関する研究 (II)(第 49 回講演大会講演大要)
- 64 法隆寺五重塔及び金堂修復に際しえられし釘に関する研究(第 49 回講演大会講演大要)
- 高周波中斷燒入に關する研究
- 8 高周波中斷燒入に關する研究(日本鐵鋼協會第 46 囘講演大會講演大要)
- アルミニウムを主成分とせるアルミニウム-珪素-鐵合金系の研究
- 示差法に據る熱分析に就て
- 高周波焼入鋼の常温におけるクリープ強さ
- コイルばね高周波焼入に関する研究
- ニッケル及び其の合金の電弧熔接に於ける酸素の影響
- ニッケル並にモネルメタルの電氣熔接
- 鐵合金製造の基礎的研究(第 1 報) : フ***マンガンに關する研究
- 電弧熔接による軸承の製作並に修理に就て
- 銅及び銅合金の電弧熔接(第 V 報) : 銅鈑とアルミニウム鈑との熔接及びアームスブロンズの熔接
- アルミニウム及其合金の電弧熔接(第 V 報) : ヂユラルミン竝にアルドライの熔接
- 軟鋼熔接棒の研究(第 III 報) : 被覆劑中の金属チタニウムが熔着金属の窒素含有量顯微鏡組織、硬度等に及す影響を述べたものである。
- 銅板の原子水素弧鎔接及金属電弧鎔接による推進機の修理(銅及銅合金の電弧鎔接(第 IV 報))
- アルミニウム及其合金の電弧鎔接(第 III 報)
- アルミニウム及びその合金の電弧鎔接(第 II 報)
- 軟鋼鎔接棒の研究(第 I 報)
- アルミニウム及びその合金の電弧鎔接(第 1 報)
- 高周波焼入した蔓巻ばねについて : その3 その他一般機械の疲労破壊の実状および対策 (ばね, ねじ, 鋼索) : 疲労破壊防止に関する座談会 (3)
- 高周波焼入の疲れ限度におよぼす影響についての一実験
- 高周波焼入した試験片の二, 三の疲れ試験の結果について
- 高周波燒入した試験片の二三の疲れ試験の結果について
- 天然並びに養殖兩鰻視器の差異に就いて