強靱鋼の低温燒戻状態に於ける切缺靱性に及ぼす試驗温度の影響
スポンサーリンク
概要
- 論文の詳細を見る
It is known that the notch strength and the notch toughness are considered to be the important characteristics for constructional alloy steels possessing higher level of strength. From the results of former investigations, one of the authors found out that low tempering temperature embrittlement of hardened alloy steels which occurred at tempering temperatures of 300∿350℃ markedly reduced the notch strength of the steels under various testing conditions, such as repeating impact, tensile and fatigue tests performed to see the properties of notched bar. This report was intended to state the studies made on the effect of testing temperatures, varying from -70 to +200℃ on Charpy impact values with two heats of Ni-Cr steels which were oilbardened and then tempered at various temperatures ranging from 100 to 450℃. From the results it was noted that the transition temperature, observed from impact value, was apparently a function of the tempering temperature, and that the tempering within the range of embrittlement caused a higher transition temperature, whereas the tempering at approx. 200℃ resulted in the lowest transition temperature. Refering this result to the results of studies made by other investigators, on the influencing factor on low-tempering-temperature embrittlement together with the factors generally affected on the transition temperature of steels, the authors suggested the possible reduction of the embrittlement by improving steel-making process, especially by means of the careful operation in the practice of deoxidation, dephosphorization, nitrogenfixation and grain-size controlling.
- 1954-01-25
著者
関連論文
- 55 含硼素強靱鋼に関する研究 (IV) : Si-Mn 鋼と Cr-B 鋼の焼入性及変態特性について(第 49 回講演大会講演大要)
- 含硼素強靱鋼に關する研究 (II)
- 含硼素強靱鋼に關する研究 (I)
- 52 含 Boron 強靱鋼に關する研究 (III) : 質量効果に及ぼす微量 Boron 添加の影響(日本鐵鋼協會第 45 回講演大會講演大要)
- 65 含 Boron 強靱鋼に關する研究 (II) : 各種構造用鋼の一般性質に及ぼす微量 Boron 添加の影響に就て(日本鐵鋼協會第 44 回講演大會講演大要)
- 強靱鋼の低温燒戻状態に於ける切缺靱性に及ぼす試驗温度の影響
- 67 構造用合金鋼の等温變態組織の電子顕微鏡的観察(日本鐵鋼協會第 47 囘講演大會講演大要)
- 4 構造用鋼の不完全燒入組織の電子顯微鏡的観察(日本鐵鋼協會第 46 囘講演大會講演大要)
- 日本鐵鋼協會第 45 回講演大會工業見學記
- ほう素鋼の熱処理と機械的性質について
- Jominy 燒入性硬度曲線に生ずる異常性について
- 110 Point Counting 法による非金屬介在物標準図の定量的検討(第 49 回講演大会講演大要)
- 超音波探傷法について : 特に製鋼工場に於ける應用例
- 37 ピクリン酸飽和水溶液による燒入鋼の一次晶顯出例(日本鐵鋼協會第 48 回講演大會講演大要)
- 各種強靭鋼の熱處理に關する研究 (II) : 強靭鋼の燒入冷却時の變態に就て
- 各種強靱鋼の熱處理に關する研究 (I)
- 37. 電氣爐鑄鐵の研究 : (第 3 報)鹽基性孤光爐に於ける各種熔解法並に材質的研究
- オーステナイト結晶粒の成長性に關する二, 三の観察
- 55 Cr-Mo 強靱鋼の低温燒戻状態における衝撃遷移特性に及ぼす Al Ti 及び B の影響(日本鐵鋼協會第 48 回講演大會講演大要)
- 39 オーステナイト結晶粒の成長性に關する二, 三の觀察(日本鐵鋼協會第 47 囘講演大會講演大要)
- 36 強靱鋼の低温燒戻状態に於ける切缺靱性に及ぼす試驗温度の影響(日本鐵鋼協會第 46 囘講演大會講演大要)
- Cr-Mo 強靭鋼の低温燒戻状態における衝撃遷移特性に及ぼす Al, Ti 及び B 添加の影響
- 51 Jominy 燒入性硬度曲線に生ずる不連續性に就いて(日本鐵鋼協會第 45 回講演大會講演大要)