特殊鑄鋼の研究 (XII) : 特殊鑄鋼の燒入, 燒戻性
スポンサーリンク
概要
- 論文の詳細を見る
The author studied on the relationship with the quench-hardening and grain size of some special cast steels which were made to add Ni, Mn, Cr, Al, Al alloys and Ca-Si in Cr-Mo cast steels. It was found that the larger the grain size was the more remarkable the quench-hardening effect become. Futher the quench-hardening effect was affected by the irreversibility of steels such as element Ni, Mn, Cr, which made decreased the transformation point of steel. It was presumed that the low carbon steel rapidly increased in quench-hardening with the addition of Ni. If the C content was large, however, the hardenability was not so marked as that of the low C steels. On the other hand, the addition of Mn and Cr had a pronounced effect than Ni. The author also investigated the relationship of such alloy steels with nonmetallic inclusions and quench-hardening. Though the quench-hardening increased with increase of Ni, Mn or Cr content, the number of inclusions was rather small and the size of it became larger. The number of inclusions increased with the addition of Fe-Si or Ca-Si, while the size of it became finer. The impact resistance decreased considerably with elevation of tempering temperature, and reached a minimum value at 300°∿400℃ (that is a first temper brittleness), while it markedly increased as tempering temperature were more elevated. In the present report the author also investigated the effect of various elements on the temper-brittleness of Cr-Mo or Cr-Mn-Si cast steels.
- 社団法人日本鉄鋼協会の論文
- 1952-05-25
著者
関連論文
- 16 80Kg/mm^2級高張力鋼の硫化水素腐食割れに関する二三の考察
- 共晶及び過共晶Al-Si合金に及ぼすBiの影響
- 黒心可鍛鋳鉄の表面焼入硬化
- 生型鑄物砂の引張強度に就いて
- 107 鑄鋼用生型鑄物砂の研究 (III) : 鑄物砂の引張強度に及ぼす砂粒形状の影響に就て(日本鐵鋼協會第 44 回講演大會講演大要)
- マグネシウム合金の研究(第 1 報) : マグネシウム-マンガン系及マグネシウム-マンガン-亞鉛系合金の機械的性質並びに耐蝕性
- 日本鐵鋼協會第 45 回講演大會工業見學記
- 7 繰返し急速加熱焼入法による鋼の機械的性貭の改善 : 微視的組織の変化
- 100 繰返し急速加熱焼入法による鋼の機械的性質の改善 : 加熱速度の影響
- 99 繰返し急速加熱焼入法による鋼の機械的性質の改善 : 結晶粒度におよぼす繰返し溶体化処理回数の影響
- (32) 高張力鋼80Kg/mm^2の熱影響部の靭性について
- 特殊鑄鋼の研究(第 1 報) : Cr-Mo 強靱鑄鋼の鑄造組織に及ぼす Si の影響
- 79 繰返急速加熱処理による鋼の機械的性貭の改善(第4報)
- 鋳鉄の燒入硬化性に就いて(第1報)
- 油砂の自硬性に関する研究
- 鑄鋼用珪石の熱傳導度について
- 中子の粘結劑に關する研究(I)
- 108 鑄鋼用珪砂の熱傳導度に就いて(日本鐵鋼協會第 44 回講演大會講演大要)
- 特殊鑄鋼の研究 (XII) : 特殊鑄鋼の燒入, 燒戻性
- 特殊鑄鋼の研究 (XI) : Cr-Mo 及び Cr-Mn-Si 鑄鋼の機械的性質に及ぼす V, Ti, Al, Si 脱酸處理の影響
- 特殊鑄鋼の研究 (X) : Mn-Si 鑄鋼の機械的性質に及ぼす Cr 及び W の影響
- 特殊鑄鋼の研究 (IX) : Cr-Mo 及び Ni-Cr-Mo 鑄鋼の機械的性質に及ぼす Mn の影響
- 特殊鑄鋼の研究 (VIII) : Cr-Mo 鑄鋼の機械的性質に及ぼす Ni の影響
- 特殊鑄鋼の研究 (VII) : 特殊鑄鋼の結晶粒度に就て
- 特殊鑄鋼の研究 (VI) : 擴散燒鈍に依る機械的性質の變化に就て
- 特殊鑄鋼の研究 (V) : 擴散燒鈍に依る鑄造組織の變化に就て
- 特殊鑄鋼の研究 (IV) : 特殊鑄鋼の鑄造組織生成の機構に就て
- 特殊鑄鋼の研究 (III) : 特殊鑄鋼の鑄造組織に就て
- 特殊鑄鋼の研究 (II) : Cr-Mo 鑄鋼の機械的性質に及ぼす Si の影響