低合金鋼に生成する島状マルテンサイトの組成および体積分率に及ぼす熱処理条件の影響
スポンサーリンク
概要
- 論文の詳細を見る
Effects of reheating temperature, corresponding to austenite single phase or ferrite-austenite two-phase region, on chemical and quantitative changes in Martensite and Austenite (M-A) constituents in a low alloy steel were examined. Reheating to austenite single phase results in bainite microstructure containing M-A constituents. Enrichment of carbon in the M-A constituents is observed. Any substantial difference in Mn content between the M-A constituents and surroundings is not observed. T_0 temperature of the steel which chemistry is equal to the M-A constituents is close to the bainite transformation finishing temperature. When the steel is reheated in the two-phase region, M-A constituents are observed in ferrite and reveal higher carbon and Mn contents than the ferrite. Carbon content of the M-A constituents decreases and Mn content increases with increasing holding time of reheating at the two-phase region. The M-A constituents observed in the materials reheated to austenite single phase region show higher carbon content than those in the steel reheated to ferrite and austenite two phase region.
- 社団法人日本鉄鋼協会の論文
- 1998-04-01
著者
関連論文
- 外面SCC実験室促進再現試験法の確立 (ラインパイプの低pH型外面応力腐食割れ挙動-1)
- API-X80グレード高周波ベンド管の開発
- CO2環境での耐溶接部選択腐食性に優れたUOE鋼管
- 耐溶接部選択腐食UOE鋼管
- 416 CO_2環境で使用されるラインパイプ溶接部の選択腐食特性
- 中心偏析に起因する水素誘起割れ発生挙動
- 応力腐食割れ感受性に及ぼす鋼のミクロ組織の影響 (ラインパイプの低pH型外面応力腐食割れ挙動-2)
- 428 横造用鋼の延性き裂発生挙動に及ぼすミクロ組織の影響
- 耐震ラインパイプの開発
- 耐震性能に優れたラインパイプNK-Hiperの変形特性
- 228 高強度ラインパイプ用鋼の加熱オーステナイト粒径および溶接熱影響部靭性におよぼすTi添加量の影響
- 高強度UOE鋼管溶接金属の靭性に及ぼす化学組成ならびに熱処理の影響
- 単位セルモデルによる2相組織鋼の変形挙動解析
- フェライト-ベイナイト2相組織鋼の変形挙動予測
- 溶接熱影響部粗粒域のTiN析出形態, 微視組織ならびに靱性に及ぼすTi含有量の影響
- 330 溶接熱影響部粗粒域靭性に及ぼすTiおよびN含有量の影響
- 314 単一熱サイクルにおける島状マルテンサイトの生成に及ぼす添加元素と熱処理条件の影響
- 低Cマルテンサイトステンレス鋼の機械的性質ならびに耐食性に及ぼす化学成分の影響
- 低合金鋼に生成する島状マルテンサイトの組成および体積分率に及ぼす熱処理条件の影響