RH 真空脱ガス装置における介在物除去機構(<特集>鉄鋼製精錬プロセスにおける界面物理化学の基礎と応用 : 平衡論の基礎と応用)

概要

論文の詳細を見る
Behavior of Al_2O_3 inclusion particles in molten steel was researched after deoxidation in RH degasser and ladle refining furnace (NK-AP). Diameter distribution of inclusion particles was measured by photo scattering method. In result, it was observed that inclusion particles were almost Al_2O_3 spheres and logarithm of number of inclusion particles were directly proportional to diameter of inclusion particles in Al-killed molten steel. It was observed that removal rate of bigger inclusion particles were faster than that of smaller inclusion particles, and particles under 3μm were hard to be removed. Because it was cleared that inclusion particles weren't removed by floating of mono-particles, model considered turbulent coagulation of inclusion particles in stirring molten steel was constructed by Saffman-Turner model and mass balance of inclusion particles. In result, behavior of inclusion particles in molten steel was explained in both of RH degasser and NK-AP by this model.
社団法人日本鉄鋼協会の論文
1998-01-01