一回冷間圧延法一方向性電磁鋼板の二次再結晶に及ぼす冷間圧延圧下率の影響

概要

論文の詳細を見る
Previouly, authors reported the effect of the reduction in cold rolling which is an important factor for secondary recrystallization of the grain-oriented electrical steel produced by the single-stage cold rolling process by varying final thickness. Then, the effect of the reduction was overlapped with that of final thickness. This time, a study has been made concerning with the effect of the reduction on secondary recrystallization by varying the thickness of hot-bands, i.e., by keeping final thickness in the same level. The following are conclusions. (1) With the increase in the reduction, at first, the size of the secondary grains gets larger, then, fine grains begin to appear among large secondary grains, and finally, fine grains occupy all part of the specimen. This phenomenon is considered to be attributed to the decrease in the nuclei of (110)[001] orientation accompanied by the increase in the reduction. (2) With the increase in the reduction, the orientations of secondary grains concentrate on the ideal (110)[001] orientation. This phenomenon is considered to be attributed to the increase in the intensity of the Σ9 coincident orientation with the ideal (110)[001] orientation in the primary matrix.
社団法人日本鉄鋼協会の論文
1991-10-01