極低ひずみ速度応力腐食試験機の試作と 2, 3 の試験結果
スポンサーリンク
概要
- 論文の詳細を見る
An extremely slow strain rate testing machine for stress-corrosion cracking (SCC), which can be continuously controlled with cross-head speeds over the range of 1.5×10^<-5>cm/s to 7.7×10^<-9>cm/s, has been newly devised and constructed. Stress corrosion behavior of Type 304 stainless steel in 143℃ 42%MgCl_2 at the potential of -0.34 V(SCE), and of Inconel 600 and Incoloy 800 in 140℃ 50%NaOH at the potential of 0 V(SCE) was examined by the newly devised testing machine. SCC was observed to occur most severely at a strain rate of 3.3×10^<-6> _s^<-1> for 304 stainless steel and 1.7×10^<-6> s^<-1> for Inconel 600 and Incoloy 800, and the susceptibility decreased at strain rates faster or slower than those for all specimens tested. For 304 stainless steel transgranular cracking was formed at the region of slower strain rates and intergranular at faster strain rates but the reverse was the case for Inconel 600 and Incoloy 800.
- 社団法人日本鉄鋼協会の論文
- 1979-02-01
著者
関連論文
- 極低ひずみ速度応力腐食試験機の試作と 2, 3 の試験結果
- 217 極低ひずみ速度応力腐食割れ試験機の試作(システム・制御試験・加熱・冷却・巻取, 加工, 日本鉄鋼協会 第 95 回(春季)講演大会)
- 軟鋼および耐候性鋼のさびについて
- 討 27 SERT 法によるオーステナイトステンレス鋼の濃厚塩化物中における応力腐食割れ(V 応力腐食割れ感受性の評価法, 第 100 回講演大会討論会講演)
- SERT法による7/3黄銅の応力腐食割れ (〔日本伸銅協会伸銅技術研究会〕第19回講演会)
- SERT法による304鋼の沸騰42%MgCl2中における応力腐食割れ伝ぱに関する研究
- SERT法による304ステンレス鋼の20%NaCl水溶液中100℃における応力腐食割れ
- SERT法による304ステンレス鋼の42%MgCl2水溶液中における応力腐食割れ挙動