鋼中チタンの状態分析法の研究

概要

論文の詳細を見る
In order to establish a method for phase analysis of titanium in steel, the chemical behaviors of various titanium compounds synthesized and those yielded in steel were investigated. Furthermore an investigation was made of the change in amount or form of the titanium compounds in steel by heat treatment. The experimental results were as follows : (1) Extraction of titanium compounds from steel was most favorably carried out by I_2-CH_3OH (10%) method. Extraction by HCl (1+1) showed a lower yield. (2) No change was seen in nitride, oxide and sulfide of titanium in steel by usual heat treatment. Titanium carbide, however, became soluble by heat treatment at about 1300℃, and reprecipitated by tempering. (3) As for the oxide form, only sesquioxide was formed in the steel specimens. (4) Titanium carbonitride could not be identified in the steels examined. (5) The procedure for phase analysis of titanium in steel is as follows : a) 1 g of sample is decomposed by 100 ml of I_2-CH_3OH(10%), under stirring, at room temperature and filtered. (Separation of metallic Ti) b) The extracted residue is treated in the 30 ml of H_2SO_4 (1+9) at 70℃ for 20 min and filtered again. (Separation of fine precipitates of carbide and nitride) c) The residue of b) is treated with 30 ml of HCl (1+1) containing HF at 70℃ for 20 min and filtered. (Coarse precipitate of nitride is determined with the filtrate, and that of carbide with the insoluble residue) d) Metallic titanium is calculated by subtraction of combined titanium fraction from the total amount which is determined with use of a separate sample.
社団法人日本鉄鋼協会の論文
1971-01-01

鋼中チタンの状態分析法の研究

スポンサーリンク

概要

著者

関連論文

スポンサーリンク