白心可鍛鋳鉄用白銑のガス脱炭
スポンサーリンク
概要
- 論文の詳細を見る
The decarburization of white pig iron such as used for making the white heart malleable cast iron was studied mainly in the exothermic atmospheres of CO-CO_2-H_2-H_2O system converted from propane. The process of decarburization of white pig iron under various heating conditions was considered by comparing the decarburization behavior of the exothermic gas containing hydrogen about 10% converted at air ratio 14 with that of the wet hydrogen containing water vapour 4% and that of the mill scale forming atmospheres of the simple CO-CO_2 system around it. The results obtained were as follows. In the flow of an exothermic gas, the decarburized amount of white pig iron was increased through a rising of propane-air ratio for producing the gas up to 10, but it was nearly independent of the variation of the air ratio in the range of 10 to 17 due to the concentration difference for carbon diffusion in the austenite phase reaching its maximum (when heated at 950℃ for 4hours in the gas cooled at 18℃ after converted at 1000℃). The decarburized weight in each atmosphere was decreased slightly in the order of the flow of wet hydrogen, the flow of the exothermic gas and the mill scale owing to the rising of the concentration difference for carbon diffusion in austenite due to the rising of surface carbon content with carbon potential of the atmospheres. It was observed that the surface structure of the decarburized layer which formed in each atmosphere in the experimental range 750 to 1100℃ was uniform single ferrite only, so that the surface carbon content was kept to within the limit of the solid solubility of carbon in α iron phase. Free cementite in the white pig tends to be stabilized and its graphitization becomes difficult with an increasing of the hydrogen amount in the decarburizing atmospheres. The rate of dissolution of graphite into unsaturated austenite as caused by decarburizing reaction was relatively small compared with that of cementite, hence the rate of decarburization was lowered with the progress of graphitization.
- 社団法人日本鉄鋼協会の論文
- 1963-07-01
著者
関連論文
- プロパンの発熱型雰囲気と鉄の平衡関係
- オーステナイトステンレス鋼の分極下での水素脆化挙動と応力腐食割れの関連性について
- 18Cr-8Ni オーステナイト系ステンレス鋼の応力腐食割れにおよぼす腐食雰囲気中の酸素の影響について(性質関係)
- 245 オーステナイト・ステンレス鋼の分極下での水素の挙動と応力腐食割れの関連性について(腐食・表面処理・高張力鋼, 性質, 日本鉄鋼協会 第 78 回(秋季)講演大会)
- オーステナイト系ステンレス鋼の応力腐食挙動におよぼす水素の影響
- 217 18Cr-8Ni ステンレス鋼の応力腐食割れと溶存酸素の関係(薄板・腐食, 性質, 日本鉄鋼協会第 77 回(春季)講演大会講演)
- 77 ガス滲炭および光輝処理に関する基確的研究(日本鐵鋼協會第 50 回講演大会講演大要)
- 19 ガス滲炭に関する研究 : 滲炭層の深さと靱性の関係について(第 53 回講演大会講演大要)
- ガス滲炭に関する研究 : 市販耐熱鋼および電熱線材の各種雰囲気に対する耐侵食性について
- 25 鋼の材質におよぼす調節雰囲気の影響(第 52 回講演大会講演大要)
- 108 ガス滲炭に関する研究 : 耐熱鋼および電熱線材の耐侵蝕性について(第 51 回講演大会講演大要)
- 78 鉄鋼の光輝処理の実施化試験(日本鐵鋼協會第 50 回講演大会講演大要)
- ガス滲炭に関する研究-1-
- 鋳鉄の黒鉛化におよぼす焼鈍雰囲気の影響
- 白心可鍛鋳鉄用白銑のガス脱炭
- 125 黒心可鍛鋳鉄の黒鉛化におよぼす焼鈍雰囲気の影響(性質, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 98 プロパンの発熱的変成雰囲気による白心可鍛鋳鉄の脱炭について(熱処理, 第 59 回(春季)講演大会講演大要)