二、三の焼割現象について
スポンサーリンク
概要
- 論文の詳細を見る
1) Quenching Cracks of alloy steels without nickel are studied by means of the repeated quenching. The tendency of quenching cracks does not decrease on account of the addition of nickel as alloying element, but that tendency decreases due to the lowering of transformation temperature by the addition of nickel. 2) A sort of quenching cracks appears especially in high carbon steel and Si-Mn-Cr steel, which is concerned to the existence of the res, dual carbides. 3) The rejecting methods of the quenching cracks of low W-Cr steel on account of machining stress are etudied. The method to reject that quenching cracks is the annealing at the temperature, at which the hardness after normalising is the lowest.
- 社団法人日本鉄鋼協会の論文
- 1947-06-20
著者
関連論文
- 88 硬度標準試片の試作の研究 (II)(日本鐵鋼協會第 47 囘講演大會講演大要)
- 4 合 Ni-Cr 鐵鑛石の磁化焙燒に關する研究 (I) : 大江山鑛石の水素による磁化焙燒(日本鐵鋼協會第 47 囘講演大會講演大要)
- 軸受鋼の熱處理の研究 (I) : 熱處理による機械的性質と寸法安定性との關係
- 37 軸受鋼の研究 (I)(日本鐵鋼協會第 45 回講演大會講演大要)
- 36 高温酸化せる鋼中の銅の擧動(日本鐵鋼協會第 45 回講演大會講演大要)
- 時計ゼンマイ材料の研究 (II)
- 時計ゼンマイ材料の研究 (I)
- 高壓交流弧光の鐵鋼分光分析への應用
- 110 高壓交流弧光の鐵鋼分光分析への應用(日本鐵鋼協會第 45 回講演大會講演大要)
- ゼンマイ材料の熱處理に關する二, 三の問題
- 含 Cu, Al 可鍛鑄鐵の研究
- 焼入性の定量的判定方法
- 最近の溶接棒
- 鐵鋼中に於けるジルコニウム
- 燒入硬度曲線の形態 (II)
- Cr 鋼滲炭層の特性とその熱處理による改善
- 燒入硬度曲線の形態 (I)
- 特殊鋼のオーステナイト粒子生長の特性 (III)
- 特殊鋼のオーステナイト粒子生長の特性 (II)
- 特殊鋼のオーステナイト粒子生長の特性 (I)
- 鋼材の火花試驗に關する研究(第 3 報)
- 無ニツケル鋼の機械試験による破斷面の形態
- 含 Cu, Cr 鑄鐵の黒鉛化の研究
- 二、三の焼割現象について
- Ni-Cr 鋼に對する Co 添加の影響
- 鋼材の火花試驗に關する研究 (II)
- 鋼材の火花試驗に關する研究(第 1 報)