An experimental examination has been performed on the adaptability of Tint Etching and Heat Tinting for 18% Ni maraging steel. Tint Etching, for which an etchant including sodium metabisulfite or sodium thiosulfate is used, and Heat Tinting at 533 K have revealed the structural component of lath martensite more clearly than the traditional approach did. The result of Tint Etching done with an etchant including potassium pyrosulfite and sulfanic acid suggests that Tint Etching is applicable to detecting segregation of alloy elements in this steel. Both methods-Tint Etching and Heat Tinting-have made a remarkable color contrast between martensite and what appears to be austenite in the sample including retained austenite.
- 大同工業大学の論文
著者
関連論文
- Fe-10%Crフェライト合金中のラ-ベス相の析出挙動に及ぼすMoとSiの影響
- Fe-10%Cr 合金におけるラーベス相析出前の初期時効現象
- 耐熱材料として開発した 12mass%Cr-15mass%Mn オーステナイト鋼の高温強度と靱性の改善
- 核融合炉第一壁構造用材料としての種々の鋼の長時間時効に伴う微細組織及び靱性の変化
- 不破関跡出土の製鉄遺物に関する冶金学的考察
- Tint EtchingならびにHeat Tintingによる鉄鋼組織の観察 : 18%Niマルエージング鋼に対する試み
- Tint EtchingならびにHeat Tintingによる鉄鋼組織の観察--18%Niマルエ-ジング鋼に対する試み
- 不破関跡出土の製鉄遺物に関する冶金学的考察