板はり構造鋼試験片の 4 点曲げひずみ挙動におけるサイクル応答差の検討
スポンサーリンク
概要
- 論文の詳細を見る
The fatigue test of surface crack propagation was conducted on the plate specimen with the small hole at a notch root in the low cycle fatigue region. The cyclic strain at a notch root was measured by strain gage and the cyclic strain behavior have been shown as the relationship between strain and number of cycles. The rate of surface fatigue crack propagation at a notch root were found from the crack length curve. It is found that the rate of surface fatigue crack propagation is expressed as the mth power of the range of strain intensity factor. Where the strain intensity factor is defined as the parameter multiplied the cyclic strain range at a notch root by root of the surface crack length. The m of mth power of the strain intensity factor range are different in the middle and in the edge of plate thickness. These experimental data and discussion have been presented.
- 長崎大学の論文
著者
関連論文
- 板試験片切欠き底の面内曲げ低サイクル疲労表面疲労き裂進展速度則の検討
- 面内曲げ切欠底の低サイクル表面疲労き裂進展速度則の検討
- 単調増加面内横荷重下の切欠き鋼試験片の降伏ひずみ挙動
- 611 面内曲げ切欠き鋼試験片の降伏ひずみ挙動(材料力学II)
- 面内曲げ切欠き試験片の表面疲労き裂進展速度則の実用式
- 低サイクル疲労強度差におよぼす平滑材と切欠き材の繰返しひずみ挙動差の詳細な考察
- 543 切欠き材の二段二重低サイクル曲げ疲労下の繰返しひずみ挙動と寿命比
- 切欠き試験片の弾塑性ひずみ挙動の研究(7) : Neuber則およびひずみ推定法の実験的検討のまとめ
- 切欠き試験片の弾塑性ひずみ挙動の研究(6) : アルミニウム材の板厚効果
- 切欠き板試験片の弾塑性ひずみ挙動の研究 : 4. 鋼材の面内曲げ
- 切欠き板試験片の弾塑性ひずみ挙動の研究 : 3.鋼およびアルミニウム合金のひずみ集中係数と塑性域寸法
- 切欠き板試験片の弾塑性ひずみ挙動の研究 : 2.鋼材のひずみ集中係数の比較考察
- 板はり構造鋼試験片の 4 点曲げひずみ挙動におけるサイクル応答差の検討
- はり構造鋼試験片の 4 点曲げひずみ挙動におよぼす降伏現象の影響
- 切欠き板試験片の繰返しひずみ挙動の研究(8) : 面内曲げ疲労
- 切欠き板試験片の弾塑性ひずみ挙動の研究 : 1.鋼材に引張り荷重作用の場合