<研究>砒〓焙焼に關する基礎的研究(第1報)
スポンサーリンク
概要
- 論文の詳細を見る
Some fun lamental experiments on the removal of arsenic from the speiss resulting from lead smelting were carried out. The composition of the speiss was Ni 32.6 Co 6.4,Cu 11.0,S 4.0,Fe 1.4,Pb 1.5,and As 40.0%. The results of the oxidizing roasting by air are reported in this paper. The change in weight of the speiss heated slowly in air was measured with a thermo-balance, and it was found that a preliminary roasting at lower temperature was unnecessary. Therefore experiments were carried out at constant temperature. The optimum roasting condition was as follows : Grain size of the charge -200 mesh ; temperature 750℃ ; blast amount 1.37 liter/hour/g. of charge ; time 60 min. It was found that only about 50% (apparent value) of arsenic in the original speiss could be removed under the above condition by one operation and the repetition of operations was without any effect.
- 東北大学の論文
- 1949-03-30
著者
関連論文
- 黄鐵鑛の解離壓に就いて
- ウランおよびトリウム化合物の高温における挙動について(第2報)二酸化ウランの酸化過程について
- ウランおよびトリウム化合物の高温における挙動について(第1報) : 硫酸ウラニル, 硫酸トリウムの熱分解について
- 硫化鑛製錬に關する基礎的研究(第11報) : 固態硫化ニツケルの水素に依る還元平衡に就いて
- 酸化ウランに関する基礎的研究(第4報) : U_yTh_O_の酸化還元平衡の測定
- 酸化ウランに関する基礎的研究(第2報) : UO_2,U_4O_9及びU_3O_8間の500-1,200℃に於ける平衡の測定
- 酸化ウランに関する基礎的研究(第1報) : UO_2,U_4O_9及びU_3O_8間の360-580℃に於ける平衡について
- ウラン鉱処理に関する研究(第2報) : 松岩鉱山産ウラン鉱浸出液よりのウラン回収
- ウラン鉱処理に関する研究(第1報) : 松岩鉱よりのウラン抽出
- UC_2の窒化
- 黒鉛の金属との両立性について
- 還元酸化の繰返えしが酸化ウラン粉末の反応活性におよぼす影響について
- 硫化ゲルマニムの解離壓に就いて
- 硫化鑛製錬に關する基礎的研究 : 熔融硫化銅に就いて
- 冶金反應平衡圖示に關する一知見
- 化學熱力學數値表
- 化學熱力學數値表
- ニッケル鑛としてのラテライトに就て
- 硫化鑛製錬に關する基礎的研究(第13報) : 固態三硫化アンチモンの水素に依る還元平衡に就いて
- 硫化鑛製錬に關する基礎的研究(第12報) : 固態三硫化蒼鉛の水素に依る還元平衡に就いて
- Ni,Co 分離の一方法に就いて
- 1941〜45年間に我國で行はれた特殊金屬製錬の研究
- 銅熔鑛爐廢ガスよりの硫黄囘收に關する物理化學的考察
- 金屬硫化物の解離壓
- 二三の製錬反應のΔF°
- 金属硫化物の解離圧
- 砒〓焙焼に關する基礎的研究(第2報)
- 砒〓焙焼に關する基礎的研究(第1報)