Effect of Immediate Quenching after As-sintered on Microstructure of WC Phase and Strength of WC-14mass%TiC-8mass%Co

スポンサーリンク

概要

• 論文の詳細を見る

• WC-14%TiC-8%Co cemented carbide of as-sintered was immediately quenched. In comparison with conventional sintered specimen, the strengths of the quenched cemented carbides were increased by 20.2%～32.8%. It was ascribed that the formation of the slip steps on WC grain's edge is induced by thermal-stresses during quenching.

• 秋田大学の論文

著者

• Goto Shoji

  Faculty Of Engineering And Resource Science Akita University

• Liu Wu

  Faculty Of Engineering And Resource Sciences Akita University

• Goto Shoji

  Faculty Of Engineering And Resource Sciences Akita University

• LU Manshan

  Faculty of Engineering and Resource Sciences, Akita University

• Lu Manshan

  Faculty Of Engineering And Resource Sciences Akita University

関連論文

• Iron Matrix Transformations and Mechanical Properties of Fe-25Cr-C-B Eutectic Cast Alloys
• SB-05-1(059) Mechanical Properties of Eutectic Fe-Cr-C Composite Alloys(Ceramic, Polymer and Composites)
• Mechanical Properties of Chromium White Cast Irons at High Temperatures
• Some Behaviors and Characteristicsof Decarburized Layer in Spheroidal Graphite Cast Iron
• Surface Hardening of Some Cast Irons with Inserted Hard Alloy Particles
• Residual Stress and Bonding Strength in the ElectricalSialon Ceramics Joint Made by Using the Brazing Metal Layer
• The Effectof Insert of WC Powder on the Surface Hardening of Non Magnetic Foundry Materials
• Effect of Immediate Quenching after As-sintered on Microstructure of WC Phase and Strength of WC-14mass%TiC-8mass%Co

スポンサーリンク