Characterization of wood-based molding bonded with citric acid
スポンサーリンク
概要
- 論文の詳細を見る
The wood-based moldings were fabricated by using only citric acid as an adhesive. Themechanical properties, water resistances, thermal properties and chemical structure were investigated. Wood powder obtained from Acacia mangium was mixed with citric acid under certain weight ratios (0-40 wt%), and each powder mixture was molded using two types of metal molds at 200 °C and 4MPa for 10 min. The modulus of rupture (MOR) and the modulus of elasticity (MOE) values of the wood-based molding containing 20wt% citric acid were 35.8 MPa and 5.4 GPa, respectively. The maximum impact strength was 0.94 kJ/m2 with the same citric acid content. The water resistance increased with increasing citric acid content, and thegood resistance to boiling water was also recognized. However, some elution of substances derived from citric acid was observed at high levels of citric acid, causing a decrease in the thermal properties. The ester linkages were detected by Fourier transform infrared spectroscopy (FT-IR), indicating that the citric acid reacted with the wood. Our results demonstrated that citric acid brings about good adhesiveness for fabricating the wood-based molding.
- Springerの論文
- 2012-02-25
著者
-
Umemura Kenji
Research Institute For Sustainable Humanosphere Kyoto University
-
Kawai Shuichi
Research Institute For Sustainable Humanosphere Kyoto University
-
Ueda Tomohide
Eidai Co., Ltd.
関連論文
- Fire protection of a laminated veneer lumber joint by wood carbon phenolic spheres sheeting
- Properties of Particleboard from Lesser-used Species I. : Albizia falcata Backer
- Durability of isocyanate resin adhesives for wood V : changes of color and chemical structure in photodegradation
- Evaluation of the fire endurance of mechanically graded timber in bending
- Water removal of wet veneer by roller pressing
- The critical stress in various stress levels of bending member on fire exposure for mechanical graded lumber
- Strength, decay and termite resistance of oriented kenaf fiberboards
- Manufacture of oriented board using mild steam treatment of plant fiber bundles
- Effects of alkali, mild steam, and chitosan treatments on the properties of pineapple, ramie, and sansevieria fiber bundles
- Characterization of the morphological, physical, and mechanical properties of seven nonwood plant fiber bundles
- Manufacture and properties of binderless particleboard from bagasse I : effects of raw material type, storage methods, and manufacturing process
- Changes in micropores in dry wood with elapsed time in the environment
- Development of binderless fiberboard from kenaf core
- Chemical changes in steam-pressed kenaf core binderless particleboard
- Development of new natural polymer-based wood adhesives III : effects of glucose addition on properties of chitosan
- Modeling of a cylindrical laminated veneer lumber II: a nonlinear finite element model to improve the quality of the butt joint
- Modeling of a cylindrical laminated veneer lumber I : mechanical properties of hinoki (Chamaecyparis obtusa) and the reliability of a nonlinear finite elements model of a four-point bending test
- Curing and degradation processes of cement-bonded particleboard by supercritical CO_2 treatment
- Kinetic analysis of color changes in cellulose during heat treatment
- Effect of moisture content on manufacturing cement-bonded particleboard using supercritical CO_2
- Characterization of wood-based molding bonded with citric acid