Incomplete Recrystallization and Subsequent Microstructural Evolution during Intercritical Annealing in Cold-rolled Low Carbon Steels
スポンサーリンク
概要
- 論文の詳細を見る
Microstructural evolution during intercritical annealing after rapid heating of cold rolled low carbon steels was investigated by EBSD and TEM. When the specimens were heated to above the Ac1 temperature before the completion of the primary recrystallization of α and then annealed, remarkable retardation of the primary recrystallization was observed, resulting in non-uniform grain size distribution of α. Because of the retardation, subgrains formed in non-recrystallized α are not consumed by recrystallized α and are thus able to gradually grow with annealing, and finally the grain size distribution of α becomes uniform. The analysis based on the rn−r0n=kt equation has shown that the subgrain growth in non-recrystallized α from the holding period of 100 to 1000 s follows n=3, indicating that the subgrain growth is controlled by the volume diffusion of Mn at α and γ interfaces. The transition of n from 3 to 2, observed at the holding time of longer than 1000 s, may be due to the gradual disappearance of the smaller γ phase at subgrain boundaries.
- 社団法人 日本鉄鋼協会の論文
- 2010-03-15
著者
-
Ogawa Toshio
Nagoya Works, Nippon Steel Corporation
-
Maruyama Naoki
Kimitsu R&D Laboratories, Nippon Steel Corporation
-
Sugiura Natsuko
Steel Research Laboratories, Nippon Steel Corporation
-
Yoshinaga Naoki
Steel Res. Laboratories Nippon Steel Corp.
-
Ogawa Toshio
Nagoya Works Nippon Steel Corporation
-
Maruyama Naoki
Kimitsu R&d Laboratories Nippon Steel Corporation
-
Sugiura Natsuko
Steel Res. Laboratories Nippon Steel Corp.
-
Sugiura Natsuko
Steel Research Laboratories Nippon Steel Corporation
-
YOSHINAGA Naoki
Steel Research Laboratories, Nippon Steel Corporation
-
Maruyama Naoki
Kimitsu R&D Lab., Nippon Steel Corporation
関連論文
- Incomplete Recrystallization and Subsequent Microstructural Evolution during Intercritical Annealing in Cold-rolled Low Carbon Steels
- Factors Affecting Texture Memory Appearing through α→γ→α Transformation in IF Steels
- Deep Drawability of Electro-deposited Pure Iron Having an Extremely Sharp //ND Texture
- Abnormal αto γ Transformation Behavior of Steels with a Martensite and Bainite Microstructure at a Slow Reheating Rate
- Comparison of the Dislocation Density in Martensitic Steels Evaluated by Some X-ray Diffraction Methods
- Incomplete Recrystallization and Subsequent Microstructural Evolution during Intercritical Annealing in Cold-rolled Low Carbon Steels
- Recrystallisation of Ti IF Steel Investigated with Electron Back-scattering Pattern (EBSP)
- Texture Evolution of IF Steel Due to Recrystallization