誘電緩和測定による高分子薄膜のガラス転移ダイナミクス
スポンサーリンク
概要
- 論文の詳細を見る
Glass transition temperature (Tg) and dynamics of thin films of polystyrene (PS) and poly(methyl methacrylate) (PMMA) are investigated using dielectric relaxation spectroscopy and related methods. In case of thin films of polystyrene, the glass transition temperature could successfully be obtained as a function of film thickness and the obtained results are consistent with those observed using other techniques such as ellipsometry. In accordance with the decrease in the glass transition temperature in thin films, the dynamics of the α-process becomes faster with decreasing film thickness and the distribution of the α-relaxation times becomes broader. In case of thin films of poly(methyl methacrylate), the thickness dependence of the α- and β-processes could be observed using the dielectric relaxation spectroscopy. Both the temperatures Tα and Tβ, at which the dielectric losses due to the α- and β-processes show a maximum at a given frequency, decrease with decreasing film thickness. Below a critical thickness, both Tα and Tβ begin to decrease rapidly with decreasing thickness. In order to investigate the positional dependence of the dynamics of the α-processes for polystyrene thin films, we utilize bilayer films, where a thin film of PS labeled with a dye is located on top of the film of unlabeled PS. For such systems, we could extract the contribution only from the upper labeled layer of PS. The glass transition temperature of the upper labeled layer between unlabeled PS layer and aluminum electrode is lower than that of the bulk labeled polystyrene. This result supports that the sample geometry commonly used for dielectric measurements of ultra thin films is the same to that used for other methods as far as the glass transition dynamics are concerned.
- 日本レオロジー学会の論文
- 2008-04-15
著者
関連論文
- Rainbow散乱の散乱角の新しい導出法
- 22pVE-7 単結晶X線回折法によるPbZrO_3の相転移の研究(22pVE 誘電体(ペロフスカイト),領域10(誘電体,格子欠陥,X線・粒子線,フォノン物性))
- 22pWE-3 高分子ガラスの低エネルギー励起の距離スケールに関する研究(22pWE 結晶化,融解,ゲル,領域12(ソフトマター物理,化学物理,生物物理))
- 12aTH-6 高分子ガラスのエイジング現象(過冷却液体・実験, 領域 12)
- 21aVA-8 誘電率,体積を通して見た高分子ガラスのエイジング現象(21aVA 領域12,領域11合同(液体液体転移・ガラス転移),領域12(ソフトマター物理,化学物理,生物物理))
- 21pRJ-2 誘電測定による高分子ガラスの非平衡緩和(領域12,領域11合同シンポジウム:緩和現象における記憶効果,領域12,ソフトマター物理,化学物理,生物物理)
- 24pRC-5 ポリスチレンガラスのエイジング現象(24pRC 過冷却液体・ガラス,領域12(ソフトマター物理,化学物理,生物物理))
- 23aZA-5 拘束系でのガラス転移
- 高分子のガラス転移とガラスダイナミクス
- 誘電緩和測定による高分子薄膜のガラス転移ダイナミクス
- 誘電測定で見る高分子薄膜のガラス転移と非平衡緩和
- 高分子薄膜におけるガラス転移・エイジングダイナミクス (ガラスのレオロジー特集号)
- 高分子薄膜におけるガラス転移・エイジングダイナミクス
- ガラスのレオロジー特集号に向けて