Effects of Alloying Elements on NaCl-induced Hot Corrosion Resistance of Stainless Steels
スポンサーリンク
概要
- 論文の詳細を見る
- 2007-07-01
著者
-
FURUKIMI Osamu
Department of Materials Science & Engineering, Kyushu University
-
Furukimi Osamu
Department Of Materials Science And Engineering Kyusyu University
-
UJIRO Takumi
Stainless Steel Research Department, Steel Research Laboratory, JFE Steel Corporation
-
Ujiro Takumi
Stainless Steel Research Dept. Steel Research Lab. Jfe Steel Corp.
-
KATO Yasushi
Stainless Steel Research Dept., Steel Research Lab., JFE Steel Corp.
-
HIRANO Masahiro
Stainless Steel Technology Sec., Stainless Steel Department, East Japan Work, JFE Steel Corp.
-
Hirano Masahiro
Stainless Steel Technology Sec. Stainless Steel Department East Japan Work Jfe Steel Corp.
-
Kato Yasushi
Stainless Steel Research Dept. Steel Research Lab. Jfe Steel Corp.
-
Furukimi Osamu
Department Of Material Science Faculty Of Engineering Kyushu University
関連論文
- Effect of Si on Precipitation Behavior of Nb-Laves Phase and Amount of Nb in Solid Solution at Elevated Temperature in High Purity 17%Cr-0.5%Nb Steels
- Corrosion Resistance of Cr-bearing Rebar to Macrocell Corrosion Caused by Concrete Cover Crack
- Corrosion Resistance of Cr-bearing Rebar in Concrete with Chloride Ion Content
- Service Life Estimation of Reinforced Concrete Structures Made Using Cr-bearing Rebars in Microcell Corrosion Environments
- A Study on the Corrosion Resistance of Cr-bearing Rebar in Mortar in Corrosive Environments Involving Chloride Attack and Carbonation
- Service Life Estimation of Concrete Structures Reinforced with Cr-bearing Rebars under Macrocell Corrosion Conditions Induced by Cracking in Cover Concrete
- Corrosion Inhibition by Cr-bearing Rebar in Concrete Due to Combined Deterioration of Carbonation and Chloride Attack
- Corrosion Resistance of Cr-bearing Rebar in Macrocell Corrosion Environments Due to Different Concentrations of Chloride Ions
- Effects of Alloying Elements on NaCl-induced Hot Corrosion Resistance of Stainless Steels
- Corrosion Resistance of Cr-bearing Rebar in Simulated Concrete Pore Solutions
- Effect of Combined Shot Treatment and Nitriding on Galling Property of Die Used for High Strength Steels