Fabrication of TiB_2 Particle Dispersed FeAl-based Composites by Self-propagating High-temperature Synthesis
スポンサーリンク
概要
- 論文の詳細を見る
FeAl–TiB2 composites have been produced from mixtures of Fe, Al, Ti and B powders using the Self-propagating High-temperature Synthesis (SHS or combustion synthesis) method. When the powder mixture was heated in vacuum to approximately 900 K, an abrupt increase in temperature was observed, indicating that the SHS reaction occurred in the powder mixture. The treating time from the start of heating to the end of the exothermic reaction was only approximately two minutes. X-ray diffraction analyses revealed that the SHS sample consisted of only FeAl and TiB2 without any elemental metals and any other compounds. Metallographic investigations using a scanning electron microscope and an electron probe microanalysis revealed that fine TiB2 particles were dispersed in FeAl matrix phase. As the volume fraction of the TiB2 particles was increased from 0.3 to 0.8 by controlling the powder mixture composition, the average TiB2 particle size increased from 1 to 7 μm and the average Vickers hardness of the composites increased from 800 to 1 600.
- 社団法人 日本鉄鋼協会の論文
- 2006-06-15
著者
-
Matsuura Kiyotaka
Div. Of Materials Sci. And Engineering Graduate School Of Engineering Hokkaido Univ.
-
Kudoh Masayuki
Division Of Materials Science And Engineering Hokkaido University
-
Matsuura Kiyotaka
Graduate School Of Engineering Hokkaido University
-
Kudoh Masayuki
Graduate School Of Engineering Division Of Materials Science And Engineering Hokkaido University
-
OBARA Yuki
Graduate School of Engineering, Hokkaido University
-
Obara Yuki
Division Of Materials Science And Engineering Hokkaido University
関連論文
- 301 Freeform Fabrication of Ti-Ni Alloy by Three Dimensional Micro-Welding
- Effect of Crucible Materials and Oxides on Static Undercooling in Molten Nickel
- Effect of Niobium on the Formation of Microstructure and Grain Boundary in Fe-Nb and Fe-C-Nb Alloys
- Solidification Behavior of Iron-Niobium and Iron-Carbon-Niobium alloys
- As-cast Austenite Grain Structure in Al Added 0.2wt% Carbon Steel
- Effects of Addition of Titanium and Boron on Columnar Austenite Grain in Carbon Steel
- Refinement of As-cast Austenite Grain in Carbon Steel by Addition of Titanium
- Numerical Model of Solidification Structure Formation in Fe-C Alloy with Peritectic Transformation
- Peritectic Transformation in Low Carbon Steels Containing High Phosphorus Concentration
- Evaluation of Crystal Multiplication at Mold Wall during Solidification of Casting
- Crystallization of Droplets in Pure Al and Al-Cu Alloy
- Combustion Synthesis of Carbide Particle Dispersed Iron Aluminide
- Formation conditions of coarse columnar austenite grain structure in peritectic carbon steels by the discontinuous grain growth mechanism
- Effects of Al and P Additions on As-cast Austenite Grain Structure in 0.2mass% Carbon Steel
- Effects of Cr Addition on Coarse Columnar Austenite Structure in As-Cast 0.2mass% Carbon Steel
- Pseudo-HIP Combustion Synthesis of FeAl-TiB_2 Composites
- Fabrication of TiB_2 Particle Dispersed FeAl-based Composites by Self-propagating High-temperature Synthesis
- Transition of solidification mode and the as-cast γ grain structure in hyperperitectic carbon steels
- Austenite Grain Growth in Peritectic Solidified Carbon Steels Analyzed by Phase-Field Simulation
- Suppression of Coarse Columnar Grain Formation in As-cast Austenite Structure of a Hyperperitectic Carbon Steel by Nb Addition