Residual Stress Measurement of Plasma-Sprayed Coatings

元データ 2003-10-15 一般社団法人日本機械学会


Residual stresses of plasma sprayed coatings, NiCr alloy, CoNiCrAlY alloy, Al_2O_3 ceramics and ZrO_2-8%Y_2O_3 ceramics, were measured in this study. SACHS method with a strain gauge was used to measure the residual stress. Type 304 stainless steel and mild steel were selected for the substrates. The results obtained were summarized as follows : 1) Tensile residual stresses were generated in plasma sprayed coatings. 2) The values of residual stress in ceramics coatings were relatively small and the values took lower than 40 MPa. 3) Tensile residual stress values of metallic alloy coatings on mild steel substrates were higher than those on type 304 stainless steel substrates. 4) Residual stresses in Low Pressure Plasma Sprayed (LPPS) -coatings were larger than those in Atmospheric Plasma Sprayed (APS) -coatings. 5) Preheating of a substrate will effectively reduce tensile residual stress in a coating.


脇 裕之 大阪電気通信大学工学部
OGURA Keiji Department of Gastroenterology, University of Tokyo
小倉 敬二 阪大基礎工
WAKI Hiroyuki Department of Mechanical Engineering, Osaka Electro-Communication University
脇 裕之 阪電通大
NISHIKAWA Izuru Department of Mechanical Engineering, Osaka Institute of Technology
KASHIHARA Yoshihiko Corporate Business Strategy Division, KYOCERA Corporation
Ogura Keiji Department Of Biology Loyola University Of Chicago
脇 裕之 大阪電気通信大学工学部第1部
Kashihara Yoshihiko Corporate Business Strategy Division Kyocera Corporation
Ogura Keiji Department of Applied Biology, Kyoto Institute of Technology
WAKI Hiroyuki Department of Mechanical Engineering, Faculty of Engineering, Iwate University