Cracking Paths During Initiation of Environmentally Assisted Cracking in High Temperature Water
スポンサーリンク
概要
- 論文の詳細を見る
- 2005-07-25
著者
-
SHOJI Tetsuo
Fracture and Reliability Research Institute, Graduate School of Engineering, Tohoku University
-
Shoji Tetsuo
Fracture And Reliability Research Institute Tohoku University Graduate School
-
Shoji T
Fracture Research Institute Graduate School Of Engineering Tohoku University
-
Sakaguchi Kazuhiko
Fracture Research And Reliability Institute Graduate School Of Engineering Tohoku University
-
Takeda Yoichi
Fracture Research Institute Graduate School Of Engineering Tohoku University
-
WANG Shengchun
Fracture Research and Reliability Institute, Graduate School of Engineering, Tohoku University
-
Wang S
Fracture Research Institute Graduate School Of Engineering Tohoku University
-
Shoji Tetsuo
Fracture And Reliability Research Institute Tohoku University
-
Takeda Yoichi
Fracture Research and Reliability Institute, Graduate School of Engineering, Tohoku University
関連論文
- Assessment of Effects of Pipe Surface Roughness and Pipe Elbows on the Accuracy of Meter Factors Using the Ultrasonic Pulse Doppler Method
- Quantitative NDE of Surface Cracks in Ceramic Materials by means of a High-Frequency Electromagnetic Wave
- Development of Pulse Ultrasonic Doppler Method for Flow Rate Measurement in Power Plant Multilines Flow Rate Measurement on Metal Pipe
- ICONE11-36615 DEVELOPMENT OF PULSE ULTRASONIC DOPPLER METHOD FOR FLOW RATE MEASUREMENTS OF POWER PLANT : Multiline flow rate measurement on metal wall pipe flow
- Measurement System of Bubbly Flow Using Ultrasonic Velocity Profile Monitor and Video Data Processing Unit, (III) Comparison of Flow Characteristics between Bubbly Cocurrent and Countercurrent Flows
- Measurement System of Bubbly Flow Using Ultrasonic velocity Profile Monitor and Video Data Processing Unit, (II) Flow Characteristics of Bubbly Countercurrent Flow
- Measurement System of Bubbly Flow Using Ultrasonic Velocity Profile Monitor and Video Data Processing Unit
- A Study on Development of Safety Monitoring System for Structure Using a Laser and 2-D Arrayed Photo Sensors(Optical Method 2)
- Development of Magnetic Camera Using 2-D Arrayed Hall Elements(NDE2)
- Effect of Temperature on the Microscopic Appearance of the Fracture Surface of Alloy 690TT under SSRT Testing(Macro-, Micro-, Meso-, and Nano-scopic Strength of Materials Relating to Microstructures)
- Mechanistic Understanding for Degraded Thermal Barrier Coatings
- Thermal Aging Embrittlement of Service-Exposed Udimet 520 Gas Turbine Blade(Student Poster Session)
- Theoretical Modeling and Experimental Study of Thermal Barrier Coatings
- B402 CHARACTERIZATION OF FRACTURE MECHANICS OF HIGH SPEED TRAIN WHEELSETS DEPENDING ON AGING EFFECTS AND ON THE LOCATION EXAMINED
- Nondestructive Evaluation of High-Temperature Oxidation Behaviour in Thermal Barrier Coatings(High Temperature Materials)
- High Temperature Oxidation Behavior of the Interface Between Thermal Barrier Coatings and MCrAlY Bond Coatings(High Temperature Materials)
- NDE of Fatigue Damage by Induced Current Focusing Potential Drop(NDE4)
- Cracking Paths During Initiation of Environmentally Assisted Cracking in High Temperature Water
- Observation of the Oxide Film Formed in High Temperature Water by Applying Electroless Ni-P Coating
- Environmentally Assisted Cracking of Simulated Alloys for Grain Boundaries of Irradiated 304 Stainless Steel in High Temperature Water Environments(Student Poster Session)
- Creep Life Prediction of Ni-Base Superalloy Used in Advanced Gas Turbine Blades by Electrochemical Method
- The Crack Tip Solution Chemistry in Sensitized Stainless Steel in Simulated Boiling Water Reactor Water Studied Using a Microsampling Technique
- Mechanical and High Temperature Oxidation Properties of Cold Sprayed CoNiCrAlY Coatings for Thermal Barrier Coating
- Thermal Aging Embrittlement of Tungsten-Alloyed 9% Cr Ferritic Steels and Electrochemical Evaluation
- Analysis of Crack Growth Kinetics and Crack Tip Strain Rates of Sensitized Type 304 Stainless Steel in Simulated Boiling Water Reactor Environment : Experiments and Theory(EAC2)
- Change in Work Function of Fatigue Damaged Surface and Its Relevance to Fatigue Failure(Student Poster Session)
- SCC Growth Behavior of Surface Cracked Specimens in High Temperature Water(EAC2)
- In-situ Measurement of Contact Electric Resistance of Oxide Films on Sensitised 304 Stainless Steel during Slow Strain Rate Test in High Temperature Water(EAC2)
- Estimation of Crack Detectability of Remotely Induced Current Potential Drop Technique Based on POD Curve(NDE4)
- Effect of Yield Strength on Stress Corrosion Crack Growth of Stainless Steel in High Temperature Water Environment(EAC2)
- The In-situ Measurement of a Local Chemical Reaction by Raman Spectroscopy : Time dependent enrichment of chloride ions on the surface of 304L stainless steel(EAC1)
- In-situ eddy current monitoring of structural components in nuclear power plants
- Small Punch Creep Behavior of Service-Exposed SUS 316 HTB Superheater Boiler Tube(High Temperature Materials)
- Crack Detection by Means of Electromagnetic Field Measurement with Micro Antennas(NDE4)
- Influence of Pre-Aging on Creep Rupture Strength of Tungsten Alloyed 9%Cr Ferritic Steel and Creep Damage Evaluation by Electrochemical Method(Special Issue on Creep and Fatigue at Elevated Temperatures)
- Impurity Removal from Carbon Saturated Liquid Iron using Lead Solvent
- The Crack Tip Solution Chemistry in Sensitized Stainless Steel in Simulated Boiling Water Reactor Water Studied Using a Microsampling Technique