Effects of SiO_2 and Al_2O_3 on the Lattice Parameter and CO Gas Reduction of CaO-containing Dense Wustite
スポンサーリンク
概要
- 論文の詳細を見る
The effects of SiO2 and Al2O3 on the lattice parameter and the initial reduction rate of CaO-containing wustite were studied at 1 273 K. Wustite plates containing 0.5-2 mass% CaO, 0.2-2 mass% SiO2 and 1 mass% Al2O3 were prepared at the mass fractions of CaO/SiO2=0.5-5. The lattice parameter of CaO–SiO2- containing wustite decreased with decreasing CaO/SiO2 ratio at a constant CaO content. This corresponded to a decrease of the dissolved content of CaO in the wustite due to a formation of CaO-FeO-SiO2 compounds. Similarly, the dissolved content of CaO decreased in CaO-SiO2-Al2O3-containing wustite. The process of CO gas reduction within the wustite phase field was traced with the lattice parameter measurement of the partially reduced samples and was analyzed with a mixed-control model of chemical reaction at the surface and the solid state diffusion in the wustite. The chemical reaction rate constant, k´, decreased with increasing the amount of SiO2 addition at a constant CaO content. The dependence of k´ on SiO2 (and Al2O3) addition was in good accordance with the change in the dissolved content of CaO in the wustite owing to the formation of the compounds containing CaO. The inter-diffusion coefficient, D, tended to decrease slightly with increasing the amount of compound.
- 社団法人 日本鉄鋼協会の論文
- 2003-03-15
著者
-
Suzuki K
Faculty Of Engineering Ibaraki University
-
Suzuki Kanae
Faculty Of Engineering Ibaraki University
-
INAMI Takashi
Faculty of Engineering, Ibaraki University
-
Inami Takashi
Faculty Of Engineering Ibaraki University
関連論文
- VIBRATIONAL TEMPERATURE OF N_2 IN THE HEIGHT RANGE OF 100-140KM
- In-situ Observation of the Reduction of Iron Oxides by Solid State Carbon in TEM
- TEM Observation of the Reduction of Wustite by Hydrogen Ion Implantation
- Effects of SiO_2 and Al_2O_3 on the Lattice Parameter and CO Gas Reduction of CaO-containing Dense Wustite
- Thermal Stability of Nanocrystalline Gold Studied by X-ray Diffraction Method
- Mechanical Properties and Thermal Stability of Nanocrystalline Gold Prepared by Gas Deposition Method
- Lattice Parameter and Redox Equilibria in CaO-containing Wustite